Abstract:Tungsten production primarily relies on scheelite, a secondary resource due to its complex ore composition and lower grade compared to high-grade wolframite. Synthetic scheelite gains significance for its low impurity content and accessibility in ongoing laboratory-based investigations. Recent advancements offer a feasible environment-friendly leaching method using a mixed solution of H 2 SO 4 and H 2 O 2 under normal pressure and moderate temperatures. However, comprehensive research on this novel method is lacking, emphasising the need for collaborative exploration and operational optimisation. The present work is to provide insights and improvements in reagent usage to promote economic and environmental sustainability. A detailed investigation into the thermal decomposition process was also conducted without compromising leaching efficiency. The findings suggest the potential for eco-friendly lixivium recycling with reduced levels of chemicals, decreasing operational costs. Notably, optimising the thermal decomposition duration to 6 hours at an L/S (mL/g) ratio of 10 enhances H 2 WO 4 crystallization. Furthermore, experiments without H 2 SO 4 supplementation highlight the system's optimisation potential. Finally, the leaching process was optimised by decreasing H 2 SO 4 concentration to 1 mol/L from 3 mol/L, increasing the temperature to 60°C, and extending the leaching duration to 120 minutes. This leads to a cost-effective synthetic scheelite leaching process with environmental benefits. La production de tungstène se fie principalement à la scheelite, une ressource secondaire en raison de la composition complexe de son minerai et de sa teneur inférieure par rapport à celle de la wolframite à haute teneur. La scheelite synthétique gagne en importance en raison de sa faible teneur en impuretés et son accessibilité dans les investigations en cours en laboratoire. Des progrès récents offrent une méthode de lixiviation réalisable et écologique utilisant une solution mixte de H 2 SO 4 et de H 2 O 2 sous une pression normale et à des températures modérées. Cependant, il manque des recherches approfondies sur cette nouvelle méthode, mettant l'emphase sur le besoin d'une exploration collaborative et d'une optimisation opérationnelle. Le travail courant vise à fournir des connaissances et des améliorations dans l'utilisation des réactifs pour favoriser la durabilité économique et environnementale. Une investigation détaillée du procédé de décomposition thermique a également été entreprise sans compromettre l'efficacité de la lixiviation. Les résultats suggèrent le potentiel d'un recyclage écologique du lixiviat avec une réduction de niveaux de produits chimiques, diminuant les coûts opérationnels. Notamment, l'optimisation de la durée de décomposition thermique à 6 heures à un rapport L/S (ml/g) de 10 améliore la cristallisation de H 2 WO 4 . De plus, des expériences sans supplémentation en H 2 SO 4 soulignent le potentiel d'optimisation du système. Finalement, on a optimisé le procédé de lixiviation en diminuant la concentration de H 2 SO 4 de 3 mol/L à 1 mol/L, en augmentant la température à 60°C et en étendant la durée de lixiviation à 120 minutes. Cela conduit à un procédé de lixiviation de la scheelite synthétique qui est économique avec des avantages environnementaux.

A Kinetic Study on the Leaching of Scheelite Sulfuric Acid Decomposition Residue with Hydrogen Peroxide

Tungsten Extraction from Scheelite Hydrochloric Acid Decomposition Residue by Hydrogen Peroxide

Efficient Leaching of Scheelite in Sulfuric Acid and Hydrogen Peroxide Solution

Selectively Extracting H2WO4 of High Purity from the H2SO4 Decomposition Product of Scheelite Through Hydrogen Peroxide Coordination Followed by Purification Using Ion-Exchange and Solvent Extraction and Thermal Decomposition

Efficient Dissolution of Tungstic Acid by Isopolytungstate Solution Based on the Polymerization Theory of Tungsten

Leaching Tungsten and Rare Earth Elements from Scheelite Through H2SO4–H3PO4 Mixed Acid Decomposition

Selectively extracting H 2 WO 4 of high purity from the H 2 SO 4 decomposition product of scheelite through hydrogen peroxide coordination followed by purification using ion-exchange and solvent extraction and thermal decomposition

Leaching Kinetics of Scheelite in Hydrochloric Acid Solution Containing Hydrogen Peroxide As Complexing Agent

Leaching Kinetics of the Pressure Decomposition of Wolframite with Sulfuric-Phosphoric Mixed Acid

Kinetics of Scheelite Concentrate Digestion with Sulfuric Acid in the Presence of Phosphoric Acid

Leaching Kinetics of Scheelite with Nitric Acid and Phosphoric Acid

A Decomposing Technique for Scheelite Concentrate and Low-Grade Scheelite Concentrate

Resin-enhanced Acid Leaching of Tungsten from Scheelite

An optimisation study for leaching synthetic scheelite in H2SO4 and H2O2 solution

Kinetics of sodium hydroxide leaching of scheelite

Acidic Decomposition of Scheelite by Organic Sodium Phytate at Atmospheric Pressure

Kinetics of Sulfuric Acid Leaching of High Silica Low-grade Zinc Oxide Ore

Scheelite Conversion in Sulfuric Acid Together with Tungsten Extraction by Ammonium Carbonate Solution

Leaching kinetics of wolframite with sulfuric-phosphoric acid

Decomposing Scheelite and Scheelite-Wolframite Mixed Concentrate by Caustic Soda Digestion

Extraction of Tungsten from Scheelite Concentrate Using a Methanesulfonic Acid- Phosphoric Acid Coleaching Process Followed by Solvent Extraction with N1923