UV-Induced Thiol-Ene "Click" Surface Grafting Polymerization on BOPP Substrate and Its Postmodifying for Hydrophilic and Antibacterial Applications

Yuqing Fan,Yuan Zhang,Lin Sheng,Dong Chen,Yuhong Ma,Changwen Zhao,Wantai Yang

DOI: https://doi.org/10.1021/acs.langmuir.3c01448

2023-01-01

Abstract:This paper proposed a novel and versatile surface modification route by integrating UV light-mediated thiol-ene "click" surface grafting polymerization and postmodification via the reactions of the surface thiol groups. At first, poly(thiol ether) layers with tunable thiol group density, up to 8.2 x 10(2) ea/nm(3) for cross-linked grafting layers, were grafted from biaxially oriented polypropylene (BOPP) film. Then, the surface -SH groups reacted with epoxy compounds to introduce quaternary ammonium salt. With the immobilized quaternary ammonium salt and coordinated Zn2+ ions, the modified film demonstrated 99.98% antibacterial rate against Staphylococcus aureusafter soaking in DI water for 21 days and in a highly alkaline environment (0.1 M NaOH aqueous solution) for 3 days, and the surface water contact angle decreased to 39 degrees. At last, the polymethacrylate chains were also successfully grafted from the surface thiol groups of the crosslinked poly(thiol ether) under visible light irradiation. With 2-(dimethyldodecylammonium) ethyl methacrylate as the grafting monomer, the modified BOPP film had shown a 99.99% antibacterial rate against both Escherichia coliand S. aureus. Meanwhile, with 2-methacryloxyethyl phosphoryl choline as grafting monomer, the modified surface showed an excellent antibioadhesion of living S. aureus, and the surface water contact angle was as low as 48 degrees.