Self-Powered Rewritable Electrochromic Display based on WO 3-x Film with Mechanochemically Synthesized MoO 3– y Nanosheets
Wenting Wu,Huajing Fang,Hailong Ma,Liangliang Wu,Qing Wang,Hong Wang
DOI: https://doi.org/10.1021/acsami.1c01959
2021-04-21
Abstract:Electrochromic displays with bistable color states provide a promising means toward transparent human–machine interfaces. However, the need for external power and the weak optical modulation in the visible light region of most electrochromic devices hinder their practical applications in displays. Here we prepare the MoO<sub>3–<i>y</i></sub>/WO<sub>3–<i>x</i></sub> films based on MoO<sub>3–<i>y</i></sub> nanosheets, which show a dark blue color that matches the response of the eye and meets visual comfort standards compared to pure WO<sub>3–<i>x</i></sub> film. By introducing the highly transparent Al<sup>3+</sup> ion hydrogel layer, a convenient electrochromic device driven by the internal chemical potential has been designed. The device based on the MoO<sub>3–<i>y</i></sub> /WO<sub>3–<i>x</i></sub> film exhibits a high optical modulation in the whole visible light range and can operate at self-powered mode with fast response speed and excellent cycle stability. Moreover, we develop an ionic writing board based on the MoO<sub>3–<i>y</i></sub>/WO<sub>3–<i>x</i></sub> film to surmount the fixed display information issue in conventional electrochromic displays. The ionic writing board exhibits excellent visual display quality and realizes arbitrary writing with a self-powered characteristic. This work provides a simple mechanochemical synthesis procedure of MoO<sub>3–<i>y</i></sub> nanosheets and an ingenious design of self-powered electrochromic devices, which will enable the development of next-generation high-performance electrochromic displays.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c01959?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c01959</a>.Table S1, FWHM of the relevant diffraction peaks in pristine/ball-milled molybdenum oxides; Figure S1, AFM images of the two-dimensional MoO<sub>3–<i>y</i></sub> nanosheets; Figure S2, EDS mapping of Mo and O elements; Figure S3. Full scan XPS of pristine MoO<sub>3</sub> and blue ball-milled MoO<sub>3–<i>y</i></sub>; Figure S4, XPS spectra of O 1s in the ball-milled MoO<sub>3–<i>y</i></sub> nanosheets; Figure S5, resistivity and conductivity of the AlCl<sub>3</sub> hydrogel electrode; Figure S6, SEM image of the structure in hydrogel; Figure S7, transmittance spectra of the MoO<sub>3–<i>y</i></sub> film; SI 8, Randles-Sevick equation; Figure S8, cyclic voltammograms of Al<sup>3+</sup> extraction of pure WO<sub>3–<i>x</i></sub> electrochromic device at different scan rates; Figure S9, digital photograph of the MoO<sub>3–<i>y</i></sub>/WO<sub>3–<i>x</i></sub> colloidal precursor, a visible laser beam proved the Tyndall effect; Figure S10, schematic illustration of electrochromic device structure; and additional references (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c01959/suppl_file/am1c01959_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology