Abstract:Thehigh-throughput workflows are developed to efficiently andreliably predict the electrical and thermal conductivities of double-transition-metal o-MXenes. We conduct the calculations for 225 double-transition-metal o-MXenes with different transition-metal combinations, surfaceterminations (-H, -F, -O, and -OH), andstructural types ("212" and "223"). Forall investigated o-MXenes, their electrical conductivitiesare found to be in the range from 10(5) up to 10(7) S/m, indicating that o-MXenes are good electronconductors. With regard to the thermal conductivity, electron thermalconduction dominates the total thermal conductivity for surface functionalized o-MXenes. In the case of intrinsic o-MXenes,lattice thermal conductivity is comparable to that of electron thermalconduction. Surface terminations show great influence on both phononand electron transport properties. It is revealed that O-terminationtends to produce semiconducting o-MXenes, while theOH-termination effectively reduces the lattice thermal conductivityof o-MXenes. Dozens of o-MXenesare predicted to be potentially excellent thermoelectric materialsfor the first time and which are found to possess Seebeck coefficientshigher than 100 & mu;V/K and have ZT values larger than 0.5 atroom temperature.

Screening of 225 Double-Transition-Metal O-Mxenes for Superior Thermoelectric Property at Room Temperature from First-Principles Electron and Phonon Calculations