Lubricant-Infused Surface Enabled by Coral-like Microstructure Based on Flocking Powder and Its Anti-icing and Anticorrosion Performance

Dandan Li,Zaiwen Lin,Qi Liu,Jiahui Zhu,Jing Yu,Jingyuan Liu,Yanhua Wang,Rongrong Chen,Jun Wang

DOI: https://doi.org/10.1021/acs.iecr.3c01666

2023-01-01

Industrial & Engineering Chemistry Research

Abstract:The application of metallic materials in low-temperatureand high-humidityenvironments suffers from two problems: corrosion and icing. To solvethese problems, lubricant-infused surfaces (LISs) have been proposed.Herein, we design an LIS and report its anti-icing and anticorrosionproperties. First, we applied the coating by spray painting with ahierarchical coral-like microstructure mixture. We then modified thesurface to obtain good water repellency with a contact angle of about151 & DEG;. The surface is then infused with silicon oil, and the slidingcharacteristics are measured. The anti-ice and deicing propertiesof the LIS retard water freezing by over 515 s and lower ice adhesionto less than 10 kPa. After 20 icing-deicing cycles, the ice adhesionof samples painted with epoxy-resin-based paint with 40% flockingpowder and infused with lubricant (called 0.4-EP-LIS) remains lessthan 40 kPa, showing that the coating is durable. The corrosion resistanceis evaluated by electrochemical measurements, which show that, despitethe different surface morphology and roughness, the anticorrosionproperties improve in the following order: only coated samples, hydrophobicsamples, and then lubricant-infused samples. Upon increasing the immersiontime, the LIS low-frequency impedance Z (0.01 Hz) decreases from 10(8) to 10(6) & omega;, and thehigh-frequency phase angle increases from -90 to -60 & DEG;.The corrosion rates of samples 0.3-EP-LIS (30% flocking powder) and0.4-EP-LIS are 1.77 x 10(-4) and 4.14 x10(-4) mm/year, respectively, which indicates excellentcorrosion resistance. Thus, the proposed LIS coating improves theanti-icing and anticorrosion performance of metallic substrates.