A Crosslinked Network Polypyrrole Coated Cobalt Doped Fe2O3@carbon Cloth Flexible Anode Material for Quasi-Solid Asymmetric Supercapacitors.

Zhiwei Li,Minglong Li,Xiaodong Wang,Ning Fu,Zhenglong Yang

DOI: https://doi.org/10.1039/d3dt01821k

IF: 4

2023-01-01

Dalton Transactions

Abstract:Iron(III) oxide (Fe2O3) exhibits a substantial theoretical specific capacitance and a broad operational voltage window, making it a prospective anode material. The crystal structure of Fe2O3 was altered through cobalt doping, and its electronic conductivity was improved by supporting it with carbon cloth (Co-Fe2O3@CC). Subsequently, a crosslinked network of polypyrrole (PPy) was synthesized onto Co-Fe2O3@CC via an ice-water bath, resulting in the formation of PPy/Co-Fe2O3@CC. This PPy nano-crosslinked network not only established three-dimensional electron transport pathways on the Fe2O3 surface but also amplified the composite material's specific surface area to 45.229 m2 g-1, thereby promoting its electrochemical performance. At a current density of 2 mA cm-2, PPy/Co-Fe2O3@CC displayed an area specific capacitance of 704 mF cm-2, a value 2.2 times higher than that of Co-Fe2O3@CC. The assembled PPy/Co-Fe2O3@CC//Ni-MnO2@CC asymmetric supercapacitor demonstrated an energy density of 1.41 mW h cm-3 at a power density of 54 mW cm-3, making the synthesized electrode material a promising candidate for flexible supercapacitors.