The Organic Ligand Etching Method for Constructing in Situ Terraced Protective Layer Toward Stable Aqueous Zn Anode.

Li,Hang Yang,Zeyu Yuan,Yicheng Tan,Yiming Zhang,Chenglin Miao,Duo Chen,Guangshe Li,Wei Han

DOI: https://doi.org/10.1002/smll.202305554

IF: 13.3

2023-01-01

Small

Abstract:The stability of aqueous Zn-ion batteries (AZIBs) is highly dependent on the reversibility of stripping/plating Zn anode. In this work, an organic ligand etching method is proposed to develop a series of in situ multifunctional protective layers on Zn anode. Particularly, the 0.02 m [Fe(CN) 6]3- etching solutions can spontaneously etch the Zn anode, creating an in situ protective layer with unique terraced structure, which blocks the direct contact between the electrode and electrolyte and increases the area for Zn2+ ions deposition. Interestingly, all elements in the organic ligands (i.e., C, N, Zn, and Fe) exhibit strong zincophilic, significantly promoting zinc deposition kinetics and enhancing 3D nucleation behavior to inhibit zinc dendrite growth. As a result, the etched Zn anode can provide as high a Coulombic efficiency of 99.6% over 1000 cycles and sustain over 400 h long-term stability at a high current density of 10 mA cm-2. As general validation, the small amount of metal cations additives (e.g., Ni2+, Mn2+, and Cu2+) can accelerate the synthesis of artificial interface layers with 3D structures and also regulate zinc deposition behavior. This work provides a new idea from the perspective of etching solution selection for surface modification of Zn metal anode. In this work, an organic ligand etching method is used to construct a multifunctional protective layer on the surface of zinc foil. Theoretical calculations and experimental tests prove that it can promote the rapid deposition of zinc ions, inhibit the side reaction and dendrite formation, and improve the cycle life and electrochemical performance of zinc-based batteries.image