Abstract:A series of poly (arylene ether sulfone)s with high molecular weight was prepared from 4-fluorophenyl sulfone, 4, 4'-biphenol and bis (4-hydroxyphenyl) sulfone with different mole ratio. Due to the large difference between the electronic effects of biphenyl fragment and phenyl sulfone fragment on the polymer, the sulfonation reaction is easily carried out on biphenyl fragments with higher electron cloud density. The sulfonic acid groups were introduced to ortho-position of the oxy ether group on the biphenyl and sulfonation degree were successfully predicted after post-sulfonation process. Sulfonated polylarylene ether sulfone (SPAES) based proton exchange membranes (PEM) were prepared by solution casting method , of which relative viscosity , ion exchange capacity (IEC) , water uptake and swell ratio , proton conductivity , oxidative stability , mechanical properties and cell performance were investigated. Relative viscosity of sulfonated copolymers was higher than 1. 2 dL/g. The sulfonated copolymers showed that titration and 'H nuclear magnetic resonance calculated value of IEC were accordingly to that of theoretical. Water uptake and swell ratio obviously increased with increasing of IEC and temperature, and the size change ratio of the thickness direction was larger than that of plane direction in the membranes. The thermal gravimetric analyse (TGA) results indicated that the PEMs have the decompose temperature at about 280 degrees C . All the PEMs showed maximum tensile strength above 50 MPa, and the elongation at break over 15% at 20 degrees C and 20% RH. Free radical oxidative stability test showed the PEMs with low IEC become brittle in Fenton' s reagent over 200 h at 20 degrees C. The proton conductivity of PEMs were increased rapidly with the increase of the IEC and temperature, for example, the conductivity of M2-SPAES(1.34 mmol/g) and M4-SPAES(1.60 mmol/g) were 68 and 89 mS/ cm at 60 degrees C in water, and 99 and 129 mS/cm at 80 degrees C in water, respectively. H-2/O-2 Fuel cell performance showed that the open circuit voltage and maximum power output were higher than 1.0 V and 0.54 W/cm(2) under 60 degrees C , 80% RH and 0.1 MPa back pressure, respectively.

Design, transport efficiency and structure-activity relationship of sulfonated poly (aryl ether ketone) proton exchange membrane based on multi-functional MOFs

Sulfonated Polyaryletherketone with Pendant Benzimidazole Groups for Proton Exchange Membranes

PEMs with High Proton Conductivity and Excellent Methanol Resistance Based on Sulfonated Poly (aryl Ether Ketone Sulfone) Containing Comb-Shaped Structures for DMFCs Applications

Efficient proton exchange membranes based on bifunctional metal–organic frameworks

Highly Proton Conductive and Mechanically Robust SPEEK Composite Membranes Incorporated with Hierarchical Metal–organic Framework/carbon Nanotubes Compound

Enhancing proton conductivity and methanol resistance of SPAEK membrane by incorporating MOF with flexible alkyl sulfonic acid for DMFC

Achieving Better Balance on the Mechanical Stability and Conduction Performance of Sulfonated Poly(ether Ether Ketone) Proton Exchange Membranes Through Polydopamine/polyethyleneimine Co-Modified Poly(vinylidene Fluoride) Nanofiber As Support

Hybrid Membrane of Sulfonated Poly(aryl Ether Ketone Sulfone) Modified by Molybdenum Clusters with Enhanced Proton Conductivity.

Constructing a long-range proton conduction bridge in sulfonated polyetheretherketone membranes with low DS by incorporating acid-base bi-functionalized metal organic frameworks

Preparation of Covalent-Ionically Cross-Linked UiO-66-NH2/Sulfonated Aromatic Composite Proton Exchange Membranes With Excellent Performance

Preparation of a Cross-linked Sulfonated Poly(arylene ether ketone) PEM with Enhanced Proton Conductivity and Methanol Resistance by Introducing Ionic Liquid Impregnated MOF.

Synthesis and Characterization of Novel Sulfonated Poly(Arylene Ether Ketone) Copolymers with Pendant Carboxylic Acid Groups for Proton Exchange Membranes

High Performance Proton Exchange Membranes with Double Proton Conduction Pathways by Introducing MOF Impregnated with Protic Ionic Liquid into SPEEK

Proton Conductivity of Proton Exchange Membrane Synergistically Promoted by Different Functionalized Metal-Organic Frameworks.

Two-Dimensional Zeolitic Imidazolate Framework/Carbon Nanotube Hybrid Networks Modified Proton Exchange Membranes for Improving Transport Properties.

Comb-shaped sulfonated poly(aryl ether sulfone) proton exchange membrane for fuel cell applications

Preparation and Characterization of Sulfonated Poly(Arylene Ether Ketone) Copolymers with Pendant Sulfoalkyl Groups As Proton Exchange Membranes

A Novel Crosslinking Organic–inorganic Hybrid Proton Exchange Membrane Based on Sulfonated Poly(arylene Ether Sulfone) with 4-Amino-phenyl Pendant Group for Fuel Cell Application

Facile one-step fabrication of sulfonated polyhedral oligomeric silsesquioxane cross-linked poly(ether ether ketone) for proton exchange membranes

Silane cross-linked network and concentrated flexible sulfoalkyl groups for forming a novel C-SPAEK membrane with enhanced methanol resistance and proton conductivity for DMFC applications

Precise Controllable Post-sulfonation for Preparation of Sulfonated Poly (arylene ether sulfone)s and Their Properties for Proton Exchange Membrane