Abstract:The influence of extrusion temperature on microstructure and mechanical properties of Mg97Y2Zn alloy have been investigated. The one-step extrusion and the two-step extrusion were conducted at the different temperatures. It was found that the extrusion temperature not only influence the microstructure of Mg97Y2Zn1 alloy but also its mechanical properties. The microstructure of the Mg97Y2Zn1 alloy processed by the one-step extrusion at 673K is non-uniform. Coarse grains elongated along the extrusion direction coexisted with small volume fraction of fine dynamic recrystallization (DRX) grains formed around secondary phase and in the vicinity of the distorted original grain boundaries. After the two-step extrusion at different temperature from 623K to 773K, the DRX process of Mg97Y2Zn1 alloy is completed and the uniform equiaxed grains were obtained. The final grain size increases with increasing deformation temperature. The alloy processed by first step extrusion exhibits highest strength by lowest elongation. After the second step extrusion, however, the strength is decreased and elongation is increased. During the second step extrusion at 623K, twins are observed at the beginning of the extrusion. The small recrystallized grains appeared along some original grain boundary areas and twinned regions. With increasing strain, the volume fraction of recrystallized grains increases progressively. However, there is no twin occurs observed at the beginning of the second step extrusion at 773K. Instead, some uniform equiaxed recrystallized grains can be observed. The small recrystallized grains appeared along some original grain boundary areas. With increasing strain, the volume fraction of recrystallized grains increases progressively and the grain size is increasing too. It seems that the DRX was brought forward at higher extrusion temperature.

Effect of Grain Size,Temperature and Strain Rate on Deformation Twinning of Mg-12Gd-3Y-0.5Zr Alloy

Statistical Analysis Of Grain-Scale Effects Of Twinning Deformation For Magnesium Alloys Under Cyclic Strain Loading

Effects of temperature and strain rate on deformation behaviors of an extruded Mg-5Zn-2.5Y-1Ce-0.5Mn alloy

Effect of twinning on the deformation behavior of an extruded Mg-Zn-Zr alloy during hot compression testing

Hot Deformation Behavior of Mg-9Y-3Zn-0.5Zr Alloy

Effect of Sm on Twinning Behavior of Mg-Gd-Y-Zr Alloy at Room Temperature Compression

Effect of Twin and Grain Size Strengthening on Tensile Properties of a Multi-Directionally Impact Forged Mg–Gd–Y Alloy

EFFECT OF TWINNING ON MECHANICAL PROPERTY AND WORKABILITY OF Mg ALLOY

Strain Rate and Texture Effects on Microstructural Characteristics of Mg-3al-1zn Alloy During Compression

Deformation mechanism of fine grained Mg–7Gd–5Y–1.2Nd–0.5Zr alloy under high temperature and high strain rates

{10–12} Twinning Relationship in Mg-Gd-Y(-Sn)-Zr Alloys under Uniaxial Compression at Room Temperature

Deformation Mechanism, Microstructure, and Mechanical Properties Evolution of Mg–Gd–Y–Zr Alloy during Cold Torsion

Investigation of the Microstructural Evolution of the As-Extruded Mg–6Zn–1Mn Alloy Sheets under High Strain Rate Tensile Loading

Compressive stress and shear stress on the deformation mechanism of Mg-13Gd-4Y–2Zn-0.5Zr alloy at different deformation temperatures

Influence of grain size on twinning behavior of WE43 magnesium alloy during room-temperature compression deformation

Effect of extrusion temperature on the microstructure and mechanical properties of Mg97Y2Zn1 alloy

Influence of Grain Size on Deformation Mechanisms in Rolled Mg–3Al–3Sn Alloy at Room Temperature

Anomalous Effects of Strain Rate on the Room-Temperature Ductility of a Cast Mg-Gd-Y-Zr Alloy

Effect of temperature on the microstructure and mechanical properties of Mg-Gd-Y-Zn-Zr alloy during the large height-to-diameter ratio upsetting and extrusion

Twining superplasticity of Mg-9Gd-4Y-0. 6Zr alloy

Effect of Cold Deformation on Microstructure and Mechanical Properties of Mg-8Gd-3Y-0.5Zr Alloy