Abstract:The FePt:C films with different volume fractions of carbon were epitaxially grown on the CrRu(200) underlayer with Pt and MgO intermediate layers. The magnetic properties and microstructure of these FePt:C films were investigated. The FePt:C films grown on Pt intermediate layer consisted of a continuous layer of FePt, with overlying granular FePt grains. The FePt:C films grown on MgO intermediate layer consisted of a granular FePt:C layer with overlying granular grains. The formation of the overlying granular FePt grains was attributed to carbon diffusion to the surface, which resulted in the second nucleation of FePt. The different interface energy and surface energy of FePt on Pt and MgO intermediate layers caused the formation of initial continuous FePt layer on Pt intermediate layer and initial granular FePt layers on MgO intermediate layer. The out-of-plane coercivity measured at room temperature increased from 10.2 to 19 kOe when C concentrations increased from 6 to 15%. Further increasing the C contents to 20% and 25% caused the decrease of coercivity to 17.2 and 14.8 kOe, respectively. The coercivity of the exchange coupling assisted FePt:C perpendicular media was indeed substantially reduced.

$L1_{0}$ FePt/Fe Exchange Coupled Composite Structure on MgO Substrates

Structural And Magnetic Properties Of A Core-Shell Type L1(0) Fept/Fe Exchange Coupled Nanocomposite With Tilted Easy Axis

Structural and magnetic properties of a core-shell type L10 FePt/Fe exchange coupled nanocomposite with tilted easy axis

The Structure and Magnetic Properties of Fept Based Perpendicular Exchange Coupled Composite Films

Microstructure And Magnetization Reversal Of L1(0)-Fept/[Co/Pt](N) Exchange Coupled Composite Films

Structural and Magnetic Properties of $\text{l}1_{\textrm {0}}$ -Fept-based Exchange Coupled Composite Films with FeRu Underlayers

Microstructure and Magnetization Reversal of L1-FePt/[Co/Pt]N Exchange Coupled Composite Films

Forc-Study of Magnetization Reversal of L1(0)-Fept Based Exchange Coupled Composite Films

Thermal Stability of FePt-Based Exchange Coupled Composite Films

L1-FePt Based Exchange Coupled Composite Films with Soft [co/ni]n Multilayers

Structural and Magnetic Properties of Perpendicular L10-FePt/[Co/Pt]N Exchange Coupled Composite Films

L1(0)-Fept Based Exchange Coupled Composite Films With Soft [Co/Ni](N) Multilayers

Development of ${\rm L}1_{0}$ FePt:C (001) Thin Films with High Coercivity and Small Grain Size for Ultra-High-Density Magnetic Recording Media

Microstructural and magnetic properties of L1 0 FePt C (0 0 1) textured nanocomposite films grown on different intermediate layers

Experimental Realization Of Graded L1(0)-Fept/Fe Composite Media With Perpendicular Magnetization

Magnetic Properties of Perpendicular Exchange Coupled Composite with A Synthesis Antiferromagnetic Sandwich Structure

Reducing the Writing Field of L1-FePt by Graded Order Parameter

Perpendicular Exchange Coupling in Tbfeco/Fept Bilayer Films

Magnetization Reversal Of L1(0) Fept/Co/Fe Trilayers

Coercivity, Microstructure and Magnetization Reversal Mechanism in Tini-Doped L1(0) Fept Thin Films

Nanogranular$L 1_0$fept:C Composite Films for Perpendicular Recording