Abstract:The 3D spherical NiO@MnO2 composites grown on Ni foam with core-shell structure were prepared by a hydrothermal process followed by a chemical bath deposition process, and then the mechanism improving the electrochemical performance of NiO by MnO2 modification were investigated by the first-principles calculations for the first time. This core-shell structure promotes an efficient contact between electrolyte and active materials, and the distinct architecture can offer fast transfer channels of ion and electrons. The initial capacitances of NiO, NiO@MnO2 (deposition time of MnO2 is 20 min), NiO@MnO2 (deposition time of MnO2 is 30 min) and NiO@MnO2 (deposition time of MnO2 is 60 min) at 10 A g(-1) are 931.6, 1064.4, 1227.2 and 766.8 F g(-1), respectively. After 10000 cycles, the reversible capacitances attenuate to 352.8, 661.0, 1089.4 and 616.6 F g(-1), respectively. NiO@MnO2 (deposition time of MnO2 is 30 min) shows the most excellent reversible capacitance at each cycle and the highest retention rates after 10000 cycles among all samples. The first-principles calculation confirms that a strong interfacial interaction between NiO and MnO2 can be generated, and then the atomic relaxations at the interface are rather small due to the well-matched interface and epitaxial bonding, resulting in a relatively small interfacial polarization of NiO@MnO2 composites during cycling. The outstanding rate capability and cycle performance of NiO@MnO2 (deposition time of MnO2 is 30 min) electrode are attributed to the synergistic effect and particular 3 D architectures.

Preparation of nano-networks of MnO<sub>2</sub>shell/Ni current collector core for high-performance supercapacitor electrodes

Preparation of nano-networks of MnO 2 shell/Ni current collector core for high-performance supercapacitor electrodes

Synthesis of MnO2/N-doped Ultramicroporous Carbon Nanospheres for High-Performance Supercapacitor Electrodes

Double‐Layer MnCo2S4@Ni‐Co‐S Core/Shell Nanostructure on Nickel Foam for High‐Performance Supercapacitor

Facile synthesis of MnO2@C@Ni(OH)2 core–shell nanowires for high-performance supercapacitor

Core-shell nanostructured MnO2@Co9S8 arrays for high-performance supercapacitors

In-Situ Synthesis of Heterostructured Carbon-Coated Co/MnO Nanowire Arrays for High-Performance Anodes in Asymmetric Supercapacitors

Construction of MnO2 nanosheets@graphenated carbon nanotube networks core-shell heterostructure on 316L stainless steel as binder-free supercapacitor electrodes

Core-shell structured MgCo2O4@Ni(OH)2 nanorods as electrode materials for high-performance asymmetric supercapacitors

Core-shell Structured Co3O4@NiCo2O4 Nanowires on Nickel Foam for Supercapacitors

Electrospinning synthesis of NiCo2O4 embedded N-doped carbon for high-performance supercapacitors

Core–Shell Structured Carbon Nanofiber-Based Electrodes for High-Performance Supercapacitors

Coaxial Carbon Nanofibers/mno2 Nanocomposites As Freestanding Electrodes for High-Performance Electrochemical Capacitors

Self-supported Core/shell Co3O4@Ni3S2 Nanowires for High-Performance Supercapacitors

Construction of hierarchical nickel cobalt sulfide@manganese oxide nanoarrays@nanosheets core‐shell electrodes for high‐performance electrochemical asymmetric supercapacitor

The Synthesis of NiCo 2 O 4 -MnO 2 Core-Shell Nanowires by Electrodeposition and Its Supercapacitive Properties.

Manganous-Manganic Oxide@Carbon Core-Shell Nanorods for Supercapacitors with High Cycle Retention

Robust Electrodes Based on Coaxial TiC/C-MnO2 Core/Shell Nanofiber Arrays with Excellent Cycling Stability for High-Performance Supercapacitors.

The Synthesis of NiCo<sub>2</sub>O<sub>4</sub>–MnO<sub>2</sub> Core–Shell Nanowires by Electrodeposition and Its Supercapacitive Properties

Construction of spherical NiO@MnO<sub>2</sub> with core-shell structure obtained by depositing MnO<sub>2</sub> nanoparticles on NiO nanosheets for high-performance supercapacitor

Preparation of nanowire-like core–shell Ni3Se4@NiCo2O4/NF composite electrodes for high-performance supercapacitors