Infrared-to-visible Upconversion Flurescence of Er{sup 3+}/yb{sup 3+}-Codoped Bismuthate Glasses

Shixun Dai,Lili Hu,Zhonghong Jiang

IF: 5.6

2005-01-01

Materials Research Bulletin

Abstract:Er{sup 3+}/Yb{sup 3+}-codoped bismuthate glasses for developing potential upconversion lasers have been fabricated and characterized. The optimal Yb{sup 3+} doping content was investigated in the glasses with different Yb{sup 3+}-Er{sup 3+} concentration ratios and the optimal Yb{sup 3+}-Er{sup 3+} concentration ratio is 5:1. Under 975 nm excitation, intense green and red emissions centered at 525, 546 and 657 nm, corresponding to the transitions {sup 2}H{sub 11/2} {yields} {sup 4}I{sub 15/2}, {sup 4}S{sub 3/2} {yields} {sup 4}I{sub 15/2} and {sup 4}F{sub 9/2} {yields} {sup 4}I{sub 15/2}, respectively, were observed at room temperature. The quadratic dependence of the 525, 546 and 657 nm emissions on excitation power indicates that a two-photon absorption process occurs under 975 nm excitation.