Following the effect of braid architecture on performance and damage of carbon fibre/epoxy composite tubes during torsional straining
Yuan Chai,Ying Wang,Zeshan Yousaf,Malte Storm,Nghia T. Vo,Kaz Wanelik,Timothy L. Burnett,Prasad Potluri,Philip J. Withers
DOI: https://doi.org/10.1016/j.compscitech.2020.108451
IF: 9.1
2020-11-01
Composites Science and Technology
Abstract:<p>The torsional performance of bi-axially braided carbon fibre reinforced polymer (CFRP) tubes as a function of braid architecture is investigated. It is found that for a given braid pattern, the 45<sup>°</sup> braided CFRP tubes have higher shear moduli and lower shear strength than the 35<sup>°</sup> braids. In general, 2/2 (regular) braided CFRP tubes exhibit both higher shear strength and higher shear modulus than 1/1 (diamond) braids. However, beyond the peak load, the shear strength of 2/2 braided CFRPs exhibits sudden, steep drops, resulting in a lower remnant shear strength than 1/1 structures after the shear strain exceeds 4.5%. Moreover, the damage evolution is monitored in-situ by synchrotron X-ray computed tomography during torsional straining. It showed that for a 2/2 structure, inter-tow debonded regions are vertically interconnected allowing rapid crack propagation and strength drops, whereas for the 1/1 braid they are distributed in a chequer board causing more gradual loss of strength. The fibre/matrix interfacial strength and tow cross-over density play key roles in the torsional failure of 1/1 and 2/2 braided CFRP tubes, as the former controls damage initiation and the latter controls damage propagation.</p>
materials science, composites