Investigation of the Nanoscale Morphology in Industrially Relevant Clearcoats of Waterborne Polymer Colloids by Means of Variable-Angle-Grazing Incidence Small-Angle X-ray Scattering
Apostolos Vagias,Qi Chen,Gert H. ten Brink,Daniel Hermida-Merino,Jurgen Scheerder,Giuseppe Portale
DOI: https://doi.org/10.1021/acsapm.9b00601
2019-01-01
ACS Applied Polymer Materials
Abstract:Soft polymer colloidal water suspensions are extremely important formulations for industrial applications such as water-based environmental-friendly coatings, paints, and adhesives. Homogeneity of the final coating at the micrometer and nanoscale is a crucial factor for optimal coating performance, such as barrier properties against solvent permeation. Here, we investigated the remnant nanostructure in slot-die-coated micrometer-sized thick clear coating films (clearcoats) of three different waterborne polymer colloids (pure soft, pure hard, and soft/hard multiphase), commonly utilized as primers in paint formulations [Mader et al. Prog. Org. Coat. 2011, 71, 123-135], using variable-angle grazing incidence small-angle X-ray scattering (GISAXS) complemented with cross-sectional atomic force microscopy (cs-AFM). After complete macroscopic drying, the coating films exhibit the presence of residual nanostructure with characteristic distance (d*) smaller than the original particle size and even smaller (<< d*) heterogeneity dimensions. These nanostructural heterogeneities (i) develop due to partial particle coalescence, (ii) are preferentially located close to the air-film interface and (iii) demonstrate the tendency to align perpendicular to the air-film interface, implying vertical gradient in hydroplasticization effects having occurred earlier during film formation. The extent and size of the nanostructural heterogeneities, driven by the slot-die coating application, strongly depend on the polymer chemistry (glass transition temperature, T-g) and the colloidal architecture. Last, solvent exposure has a significant impact on the nanostructure, causing the removal of these heterogeneities and leading to a more strongly coalesced film.