Abstract:A series of laboratory experiments were conducted to investigate the effect of freeze–thaw (FT) cycles on mechanical properties and chloride permeability of concrete with the strength class of C30 in this paper. The mechanical property tests were performed on the specimens subjected to 0, 5, 15, 30, 50, 75 and 100 standard FT cycles to determine the compressive strength, normalized dynamic elastic modulus (NDEM) and mass loss. Also, the chloride natural diffusion tests of concrete specimens, after 0, 5, 15, 30 and 50 FT cycles, were conducted in a self-design tidal cycling simulation device to investigate the chloride ingress into concrete in marine environment of tidal zone. Based on the Fick's second law, a time-dependent model was developed to predict the chloride profiles of frost-damaged concrete. Additional FT cycling tests at different minimum temperatures of freezing process (−4 and −11 °C) and the chloride natural diffusion tests were conducted to study the effect of minimum temperature on the chloride diffusion in concrete. The experimental results revealed the significant influence of FT action on the mass loss, compressive strength and NDEM. After 50 FT cycles, the mean of NDEM dropped to 60%, indicating that the specimen was destroyed by FT action. With the decrease of minimum freezing temperature, the loss of NDEM increased apparently, performing a good linear relation. A substantial effect of FT damage on the chloride profiles was observed: compared to the counterparts of the control groups without being exposed to FT attack, chloride concentration was larger for the frost-damaged concrete, and this difference increased with the extension of exposure duration. A linear relation between the apparent chloride diffusion coefficient and the loss of NDEM was also obtained regardless of the exposure time. Moreover, it was found that the proposed model was applicable for the prediction of chloride profiles in concrete subjected to FT cycles at different minimum freezing temperatures. In other words, the proposed model can be used to describe the chloride ingress into frost-damaged concrete, regardless of the cause of the damage (due to the number of FT cycles or the minimum freezing temperature).

Model of Chloride Ingress into Concrete in Cold Regions

A Numerical Study on Chloride Diffusion in Freeze-Thaw Affected Concrete

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Study On Relationship Between Chloride Diffusion In Concrete And Time

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Diffusion Model Of Chloride Ion In Concrete And Its Verification

Modeling of chloride ions diffusion in cracked concrete

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

MECHANISM AND MATHEMATIC MODELING OF CHLORIDE PERMEATION IN CONCRETE UNDER UNSATURATED STATE

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

A Multi-Phase Model for Predicting the Effective Diffusion Coefficient of Chlorides in Concrete

Erosion model of chloride ion in concrete and its verification

Chloride Ion Ingress Distribution Within an Alternate Wetting-Drying Marine Environment Area

Influence of Initial Curing Conditions and Exposure Environments on Chloride Migration in Concrete Using Electrochemical Method

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

Experimental studies on the chloride ion permeability of concrete considering the effect of freeze–thaw damage

Chloride Ion Corrosion Pattern and Mathematical Model for C60 High-Strength Concrete after Freeze-Thawing Cycles

Macroscopic and Mesoscopic Deterioration Behaviors of Concrete under the Coupling Effect of Chlorine Salt Erosion and Freezing–Thawing Cycle

New Approach to Predict the Distribution of Chloride Concentration in Concrete

Reactive Transport Modelling of Concrete Subject to De-Icing Salts and Atmospheric Carbonation

Chloride Ion Distribution in Concrete of Dry-Wet Cycling Region along Elevated Altitude