Abstract:The natural polysaccharide-based hydrogels have gained significant interest to use as 3D scaffolds for bone repair and reconstruction owing to their excellent biocompatibility, biosafety, and biodegradability. Yet, these hydrogels have major obstacles in terms of insufficient properties such as mechanical, osteogenic, angiogenic, and biomineralization. Therefore, this study mainly aims to develop an innovative water-soluble phosphate functionalized chitosan (CSMAP) through consequent modification with methacrylic anhydride (MA), then alteration by phosphonopropionic acid (P). Further, a novel photocrosslinked composite hydrogel was fabricated with a combination of CSMAP and synthesized strontium phosphosilicate (SPS, Sr5(PO4)2SiO4) bioceramic nanoparticles with a photoinitiator under UV irradiation. The various concentrations of nanosized SPS particles (0.5, 2.5, 5, and 10 mg/mL) were incorporated into the CSMAP matrix and the swelling, mechanical, morphological, physiochemical, osteogenic, angiogenic properties were investigated. The CSMAP-SPS composite hydrogels possessed a well-arranged porous network structure. The composite hydrogel was restricted to swell in distilled water with the increased concentration of SPS particles. The compressive strength and modulus of CSMAP hydrogel were improved by the inclusion of SPS particles. The bioactive Sr, P, and Si ions were released from CSMAP-SPS hydrogels in a sustained and controlled manner at a non-toxic level. The composite hydrogels promoted in vitro amorphous apatite deposition, revealing a superior biomineralization activity. In vitro results demonstrated that the composites hydrogels showed no toxicity to preosteoblast MC3T3-E1 cells, induced MC3T3-E1 osteogenic differentiation with detection of bsp, ocn and opn osteogenic genes, and also promoted the endothelial tube formation with increased capillary length, branch points, and angiogenic gene vegf expression. Thus, the obtained results proved that the fabricated novel CSMAP-SPS hydrogel could act as an attractive candidate for bone regeneration.

Influences of Mesoporous Magnesium Silicate on the Hydrophilicity, Degradability, Mineralization and Primary Cell Response to a Wheat Protein Based Biocomposite

3D Printing Novel Porous Granule-Type Bioceramics Via Magnesium Tuning Biological Performances Beneficial for Implantation and Clinical Translation

Influences of Doping Mesoporous Magnesium Silicate on Water Absorption, Drug Release, Degradability, Apatite-Mineralization and Primary Cells Responses to Calcium Sulfate Based Bone Cements.

Biodegradation and Cell Behavior of a Mg-Based Composite with Mesoporous Bioglass

3D Printing Magnesium-Doped Wollastonite/β-Tcp Bioceramics Scaffolds with High Strength and Adjustable Degradation

Preparation and characterization of bioactive mesoporous wollastonite - Polycaprolactone composite scaffold

Simultaneous Mechanical Property and Biodegradation Improvement of Wollastonite Bioceramic Through Magnesium Dilute Doping

The effects of surface bioactivity and sustained-release of genistein from a mesoporous magnesium-calcium-silicate/PK composite stimulating cell responses in vitro, and promoting osteogenesis and enhancing osseointegration in vivo

Effect of biocomposite mediated magnesium ionic micro-homeostasis on cell fate regulation and bone tissue regeneration

Effect of magnesium and calcium ions on the strength and biofunctionality of GelMA/SAMA composite hydrogels

In‐situ Enzymatic Reaction Generates Magnesium‐Based Mineralized Microspheres with Superior Bioactivity for Enhanced Bone Regeneration

Advanced bredigite-containing magnesium-matrix composites for biodegradable bone implant applications

A new composite fabricated from hydroxyapatite, gelatin-MgO microparticles, and compatibilized poly(butylene succinate) with osteogenic functionality

Macro-mesoporous Composites Containing PEEK and Mesoporous Diopside As Bone Implants: Characterization, in Vitro Mineralization, Cytocompatibility, and Vascularization Potential and Osteogenesis in Vivo.

A tailored hydroxyapatite/magnesium silicate 3D composite scaffold: Mechanical, degradation, and bioactivity properties

Interfacial Compatibilization into PLA/Mg Composites for Improved In Vitro Bioactivity and Stem Cell Adhesion

Porous calcium silicate bioactive material-alginate composite for bone regeneration

Biopolymer-coated magnesium-alloy-based multi-functional bio-nanocomposite scaffolds

Peptide-laden Mesoporous Silica Nanoparticles with Promoted Bioactivity and Osteo-Differentiation Ability for Bone Tissue Engineering.

A Novel Photocrosslinked Phosphate Functionalized Chitosan-Sr5(PO4)2SiO4 Composite Hydrogels and in Vitro Biomineralization, Osteogenesis, Angiogenesis for Bone Regeneration Application

Development of degradable and bioactive composite as bone implants by incorporation of mesoporous bioglass into poly(l-lactide)