Structural and Magnetic Properties of the Layered Manganese Oxychalcogenides (Lao)2mn2se

Ronghua Liu,J. S. Zhang,Peng Cheng,X. G. Luo,Jianghua Ying,Y. J. Yan,Meigen Zhang,A. F. Wang,Ziji Xiang,G. J. Ye,Xianhui Chen

DOI: https://doi.org/10.1103/physrevb.83.174450

IF: 3.7

2011-01-01

Physical Review B

Abstract:The new layered manganese oxychalcogenides (LaO)${}_{2}$Mn${}_{2}$Se${}_{2}$O and (BaF)${}_{2}$Mn${}_{2}$Se${}_{2}$O, isostructural to (LaO)${}_{2}$Fe${}_{2}$Se${}_{2}$O, were synthesized by solid state reaction method. The single crystals of the former compound were also successfully grown using fusion method. The polycrystalline samples show the semiconducting behavior with the activation energy gaps of about 278 and 416 meV for (LaO)${}_{2}$Mn${}_{2}$Se${}_{2}$O and (BaF)${}_{2}$Mn${}_{2}$Se${}_{2}$O, respectively. The magnetic susceptibility and specific heat indicate an antiferromagnetic (AFM) transition at around 160 $\ifmmode\pm\else\textpm\fi{}$ 1 K for the former compound and 100 $\ifmmode\pm\else\textpm\fi{}$ 1 K for the latter compound. The strong anisotropic magnetic properties below ${T}_{N}$ of the former compound suggests a long-range canted AFM ordering. A broad maximum of the susceptibility can be observed for the two compounds at high temperatures of 360 and 210 K, respectively, suggesting that strong frustrated magnetic correlation gives rise to low-dimensional AFM or short-range ordering at high temperatures in these rare transition metal oxychalcogenides with an AFM checkerboard spin lattice.