Abstract:Electron beam welding–brazing (EBWB) was applied to join TA2 and 2024Al alloys with Al-Mg filler wire. The effect of gap clearance on interfacial microstructures and mechanical properties of the butt Ti/Al joint was discussed. Three types of intermetallic compound (IMC) layers, including discontinuous cellular shape, continuous serrated shape, and discrete club shape, were presence at the TA2 interface. With the increase of gap clearance, the thickness of the IMC layer increased gradually, and the morphology of IMC layer changed from cellular shape to serrated shape and ultimately to club shape. The IMC layer was mainly TiAl3 compound, while the weld zone (WZ) comprised the predominant α-Al and bits of Al-Cu eutectic. The tensile strength of Ti/Al joint first increased and then decreased with the increased gap clearance. When the gap clearance of the butt configuration was 0.4 mm, the Ti/Al joint 3# exhibited the highest strength (316.4 MPa), about 73.7

Effect of Gap Clearance on Microstructure and Mechanical Properties of Electron Beam Welding–Brazing Ti/Al Butt Joint with Al-Mg Filler Wire