Room Temperature Synthesis and Photocatalytic Activity of Magnetically Recoverable Fe 3 O 4 /biocl Nanocomposite Photocatalysts

Congwei Tan,Gangqiang Zhu,Mirabbos Hojamberdiev,Cai Xu,Jia Liang,Pengfeng Luo,Yun Liu

DOI: https://doi.org/10.1007/s10876-013-0602-3

2013-01-01

Journal of Cluster Science

Abstract:Magnetically recoverable Fe 3 O 4 /BiOCl nanocomposite photocatalysts were fabricated by a simple chemical coprecipitation method at room temperature. The amount of Fe 3 O 4 incorporated into BiOCl was varied from 0 to 20 wt%. The as-synthesized samples were characterized by X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, UV–Vis diffuse reflectance spectroscopy, and vibrating sample magnetometer. The obtained results show that the as-synthesized samples mainly contain both crystalline phases (Fe 3 O 4 and BiOCl) and are composed of flower-like nanostructures. Compared to UV light-responsive BiOCl, all the nanocomposite photocatalysts show a strong light absorbance in the range of 250–800 nm, demonstrating that the Fe 3 O 4 /BiOCl nanocomposites can respond to visible as well as UV light. Moreover, visible light absorbance was increased with the increase in the Fe 3 O 4 amount in the composite. The photocatalytic activity of nanocomposite photocatalysts was evaluated by the photodegradation of Rhodamine B (RhB) over the samples under visible light irradiation. The 10 wt% Fe 3 O 4 /BiOCl nanocomposite photocatalyst shows the highest photocatalytic efficiency among the samples. The Fe 3 O 4 /BiOCl nanocomposite photocatalyst was stable under visible light irradiation to efficiently degrade RhB molecules after five cycles and could be easily recovered with a magnet after each cycle.