Nonmagnetic Mg 2+ -Induced Cation Occupation and Magnetic Properties of Magnetite Nanocrystals

Yibo Liu,Xinyuan Li,Xianfeng Yang,Shuai Chang,Juan Feng,Xinghua Li,Xiuhong Zhu,Yan Zong,Xin Liu,Xinliang Zheng

DOI: https://doi.org/10.1007/s10854-022-07746-4

2022-01-01

Journal of Materials Science Materials in Electronics

Abstract:Understanding the substitution on the cation occupation situation of spinel ferrites is of great significance for tailoring their magnetic properties and expanding the applications. As a necessary and constant element in human body, nonmagnetic Mg 2+ with good biocompatibility can induce softer magnetism and larger DC hysteresis loss, which is beneficial for biomedicine. However, the occupancy of Mg 2+ in Fe 3 O 4 is still unclear. Herein, Mg-doped magnetite (Mg x Fe 3-x O 4 , 0 ≤ x ≤ 0.4) nanocrystals were fabricated through thermal decomposition. The well-dispersed Mg x Fe 3-x O 4 nanocrystals show irregular hexagonal shape with a particle size of about 13–17 nm, indicating that Mg 2+ substitution has ignorable influence on the particle size. Magnetic investigations reveal that all the Mg x Fe 3-x O 4 nanocrystals show soft ferrimagnetic feature with small coercivities at room temperature. The saturation magnetization values decrease first and then slightly increase, by improving the doping amount of Mg 2+ . Compared to Fe 3 O 4 nanocrystals ( T v ≈ 108 K), the slight improved Verwey transition in Mg x Fe 3-x O 4 nanocrystals ( T v ≈ 114 K) indicates that Mg 2+ may affect the electronic transition between Fe 2+ and Fe 3+ in octahedral sublattices. Mössbauer spectra show that Mg 2+ is existed in both the tetrahedral and octahedral sites, but it prefers to occupy the octahedral sites. The proportion of Mg 2+ in tetrahedral sites becomes larger by increasing the doping amount. This work shows that nonmagnetic Mg 2+ can induce the cation redistribution and tailor the magnetic properties of spinel ferrites.