PVDF-based nanoceramic composite for improved SDBD thruster at low

Liwe Zhou,Liqiu Wei,Zhou Yang,Jingjing Li,Desheng Zhou,Hong Li,Jingfeng Tang,Yongjie Ding

DOI: https://doi.org/10.1016/j.vacuum.2023.112234

IF: 4

2023-01-01

Vacuum

Abstract:The dielectric properties of a dielectric material significantly affect the gas-solid interface discharge character-istics of the surface dielectric barrier discharge (SDBD) and surface space charge accumulation. In this study, new high dielectric composite dielectrics were prepared from barium calcium zirconate titanate nanoceramic parti-cles (BZCT-NPs) using olyvinylidene luoride (PVDF) as a matrix. The impact of the amount of BZCT-NPs incorporated in the dielectric was investigated, and the influence mechanism of the new dielectric on the per-formance of SDBD ion wind thrusts was studied. Dielectrics with 3% (v/v) and 5% (v/v) BZCT-NPs/PVDF had significantly higher dielectric constants, 111% +/- 2% and 135% +/- 5%, respectively, compared to dielectrics made only of PVDF. The loss angle tangent values increased by 673% +/- 33% and 707% +/- 33%, respectively. The discharge charge increased by 54% +/- 4% and 108% +/- 13%, and the discharge time in one cycle increased by 23% +/- 6% and 13% +/- 4%, respectively. The single-point maximum wind speeds increased by 23.2% and 8.7%, respectively. The maximum thrust-to-power ratio of the 0% (v/v), 3% (v/v), and 5% (v/v) BZCT-NP dielectrics were 1060 mu N/kW, 3120 mu N/kW, and 2436 mu N/kW, respectively. Interestingly, the minimum operating voltage of the thrusters decreased with increasing volume fraction of BZCT-NP, while the thrust-to-power ratio of the thruster increased significantly with higher levels of nanoceramic particles. The starting operating voltage of the 3% (v/v) BZCT-NPs/PVDF dielectric decreased by approximately 35% and 50% compared to the 5% (v/v) BZCT-NPs/PVDF and PVDF dielectrics, respectively, while the maximum thrust-to-power ratio increased by 194.3% and 129.8%, respectively.