Microstructure and Electromagnetic Properties of Cu-Ti Co-doped M-type BaFe12O19 Hexaferrites

Wang Chunman,Peng Zhijian,Wang Chengbiao,Fu Xiuli
2018-01-01
Rare Metal Materials and Engineering
Abstract:Using BaCO3, Fe2O3, CuO and TiO2 powders as raw materials, BaFe12-2xCuxTixO19 (x=0.00, 0.05, 0.10, 0.15 and 0.20) ferrites were fabricated at the optimum temperature of 1200 degrees C by a conventional solid-state-reaction sintering method. The co-doping effect of Cu2+-Ti4+ on the microstructure and magnetic properties of the as-prepared ferrites was investigated. The results show that the doped Cu2+-Ti4+ can enter the lattice of BaFe12O19, and no second phase is observed in the doped samples. With the increase of doping amount of Cu2+-Ti4+ ions, the coercivity of the prepared samples decreases from 204.46 kA/m to 86.82 kA/m and the saturation magnetization fluctuates somewhat between 54.61 and 58.42 A.m(2)/kg. With increasing doping amount of Cu-Ti ions, the dielectric constant increases first and then decreases, but the change of dielectric loss is very slight.
What problem does this paper attempt to address?