Abstract:Pointdefects play a critical role in the transport propertiesof Mg3Sb2-based thermoelectric materials. However,the determination of point defects is rather challenging. Herein,Mg3Sb2 single crystals were prepared by theself-flux method with the Sb flux (p-type sample) and Mg flux (n-typesample). The crystal structure as well as the atomic occupancy parametersof these samples were determined by single-crystal and synchrotronpowder X-ray diffractions. Comparison between the experimental andcalculated Fourier electron density maps generated by single-crystaldata indicates the existence of Mg interstitials [1/3, 2/3, 0.38(3)]and vacancies at the Mg2 sites [2/3, 1/3, 0.8653(3)] in the n-typesample and Mg vacancies at both the Mg1 and Mg2 sites in the p-typesample. In addition, differences in the peak positions and intensitiesof the two types of Mg-Sb vibration modes in Raman spectrawere observed between different Mg3Sb2 crystals,which suggests that point defects can impact the vibration modes.

Identifying the Point Defects in Single-Crystalline Mg3Sb2