Abstract:Phosphoserine is a ubiquitous molecule found in numerous proteins and, when combined with alpha-tricalcium phosphate (α-TCP) powder, demonstrates the ability to generate an adhesive biomaterial capable of stabilising and repairing bone fractures. Design of Experiments (DoE) approach was able to optimise the composition of phosphoserine-modified calcium phosphate cement (PM-CPC) demonstrating that the liquid:powder ratio (LPR) and quantity of phosphoserine (wt%) significantly influenced the handling, mechanical, and adhesion properties. Subsequently, the DoE optimisation process identified the optimal PM-CPC formulation, exhibiting a compressive strength of 29.2 ± 4.9 MPa and bond/shear strength of 3.6 ± 0.9 MPa after a 24 h setting reaction. Moreover, the optimal PM-CPC composition necessitated a mixing time of 20 s and displayed an initial setting time between 3 and 4 min, thus enabling homogenous mixing and precise delivery within a surgical environment. Notably, the PM-CPC demonstrated a bone-to-bone bond strength of 1.05 ± 0.3 MPa under wet conditions, coupled with a slow degradation rate during the first five days. These findings highlight the ability of PM-CPC to effectively support and stabilise bone fragments during the initial stages of natural bone healing. The developed PM-CPC formulations fulfil the clinical requirements for working and setting times, static mechanical, degradation properties, and injectability, enabling surgeons to stabilise complex bone fractures. This innovative bioinspired adhesive represents a significant advancement in the treatment of challenging bone injuries, offering precise delivery within a surgical environment and the potential to enhance patient outcomes. STATEMENT OF SIGNIFICANCE: This manuscript presents a noteworthy contribution to the field of bone fracture healing and fixation by introducing a novel phosphoserine-modified calcium phosphate cement (PM-CPC) adhesive by incorporating phosphoserine and alpha-TCP. This study demonstrates the fabrication and extensive characterisation of this adhesive biomaterial that holds great promise for stabilising and repairing complex bone fractures. Design of Experiment (DoE) software was used to investigate the correlations between process, property, and structure of the adhesive, resulting in a cost-effective formulation with desirable physical and handling properties. The PM-CPC adhesive exhibited excellent adhesion and cohesion properties in wet-field conditions. This research offers significant potential for clinical translation and contributes to the ongoing advancements in bone tissue engineering.

Design and Improvement of Bone Adhesive in response to Clinical Needs

Biodegradable and Biocompatible Adhesives for the Effective Stabilisation, Repair and Regeneration of Bone

Polyacrylic acid-reinforced organic-inorganic composite bone adhesives with enhanced mechanical properties and controlled degradability

Bone adhesive materials: From bench to bedside

Current State of Bone Adhesives—Necessities and Hurdles

Strong and bioactive bioinspired biomaterials, next generation of bone adhesives

Overcoming the Dilemma of In Vivo Stable Adhesion and Sustained Degradation by the Molecular Design of Polyurethane Adhesives for Bone Fracture Repair

Bioinspired Mineral-Organic Bone Adhesives For Stable Fracture Fixation And Accelerated Bone Regeneration

Flexible Osteogenic Glue as an All‐In‐One Solution to Assist Fracture Fixation and Healing

Biodegradable dual-crosslinked adhesive glue for fixation and promotion of osteogenesis

Bioactive Pore-Forming Bone Adhesives Facilitating Cell Ingrowth for Fracture Healing

Research Progress in the Bonding Properties of Medical Bone Adhesives

Bone Adhesives: Bioactive Pore‐Forming Bone Adhesives Facilitating Cell Ingrowth for Fracture Healing (adv. Mater. 10/2020)

Bio-Based Adhesives for Orthopedic Applications: Sources, Preparation, Characterization, Challenges, and Future Perspectives

Multi-objective property optimisation of a phosphoserine-modified calcium phosphate cement for orthopaedic and dental applications using design of experiments methodology

A Mechanically Reinforced Super Bone Glue Makes a Leap in Hard Tissue Strong Adhesion and Augmented Bone Regeneration

Hydrophilic competent and enhanced wet-bond strength castor oil-based bioadhesive for bone repair

Biodegradable Implants for Internal Fixation of Fractures and Accelerated Bone Regeneration

Local bone metabolism balance regulation via double-adhesive hydrogel for fixing orthopedic implants

Recent Advances in Biomaterials for the Treatment of Bone Defects

Advances in the Study of Bionic Mineralized Collagen, PLGA, Magnesium Ionomer Materials, and Their Composite Scaffolds for Bone Defect Treatment