Complementary Effect of Ti and Ni Incorporation in Improving the Electrochemical Performance of a Layered Sodium Manganese Oxide Cathode for Sodium-Ion Batteries
Zheng-Yao Li,Xiaobai Ma,Hao Guo,Linfeng He,Yuqing Li,Guohai Wei,Kai Sun,Dongfeng Chen
DOI: https://doi.org/10.1021/acsaem.1c00527
IF: 6.4
2021-05-19
ACS Applied Energy Materials
Abstract:Exploiting high-performance cathodes is still in need for sodium-ion batteries, which is critical to promote their commercialization. Layered sodium manganese oxide cathodes show low cost and natural abundance but suffer from poor cycling life and rate capacity. Herein, electrochemically inert Ti<sup>4+</sup> and active Ni<sup>2+</sup> are used to replace some Mn ions in Na<sub>0.62</sub>MnO<sub>2</sub>, and neutron power diffraction results demonstrate a negligible change in the sizes of the metal layer and Na-ion layer in the structure. Although Na<sub>0.62</sub>[Ni<sub>0.12</sub>Ti<sub>0.12</sub>Mn<sub>0.76</sub>]O<sub>2</sub> and Na<sub>0.62</sub>MnO<sub>2</sub> share the same Na content in pristine materials and theoretical capacity, the improved performance of Na<sub>0.62</sub>[Ni<sub>0.12</sub>Ti<sub>0.12</sub>Mn<sub>0.76</sub>]O<sub>2</sub> stems from the suppressed phase transitions and ordering process, alleviated Jahn–Teller distortion, and a high Na utilization of 73.8% compared with 62.2% for Na<sub>0.62</sub>MnO<sub>2</sub>. Ti<sup>4+</sup> stabilizes the crystal structure and hinders the multiple phase transitions and Na<sup>+</sup>/vacancy ordering upon cycling, and Ni<sup>2+</sup> improves the working voltage and compensates the capacity loss associated with decreased Mn<sup>3+</sup> content. Na<sub>0.62</sub>[Ni<sub>0.12</sub>Ti<sub>0.12</sub>Mn<sub>0.76</sub>]O<sub>2</sub> exhibits an average working voltage of about 3.5 V, a great rate capability, and cycling stability of 76.8% capacity retention after 120 cycles in the voltage range of 2.5–4.5 V. The work offers an insight into enhancing advanced layered sodium manganese oxide cathode materials for sodium-ion batteries.This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels