Bio-Sourced, High-Performance Carbon Fiber Reinforced Itaconic Acid-Based Epoxy Composites with High Hygrothermal Stability and Durability

Kaixuan Xiao,Yuan Fang,Zhaodi Wang,Nannan Ni,Ziqian Liu,Soochan Kim,Zongfu An,Zhiyi Lyu,Yahong Xu,Xin Yang
DOI: https://doi.org/10.3390/polym16121649
IF: 5
2024-06-12
Polymers
Abstract:Thermosetting polymers and composites are a class of high-performance materials with significant industrial applications. However, the widespread use of thermosets and their composites generates large quantities of waste and leads to serious economic and environmental problems, there is a critical need in the elaboration of sustainable composite materials. Here, we propose a method to prepare sustainable carbon fiber reinforced composites with different degrees of greenness by blending environmentally friendly EIA with DGEBA in different ratios, and the properties compared with a well-known commercial petroleum-based epoxy resin. The prepared carbon fiber reinforced polymer (CFRP) composites with different degrees of greenness had excellent dimensional stability under extreme hygrothermal aging. After aging, the green CFRP composite T700/EIA-30 has higher strength and performance retention than that of petroleum-based CFRP composites. The higher hygrothermal stability and durability of EIA-based epoxy resins as compared with BPA-based epoxy resins demonstrated significant evidence to design and develop a novel bio-based epoxy resin with high performance to substitute the petroleum-based epoxy resin.
polymer science
What problem does this paper attempt to address?
### Problems the paper attempts to solve This paper aims to solve the economic and environmental problems caused by a large amount of waste generated during the use of traditional epoxy - based composites. Specifically, the paper proposes a method to prepare carbon - fiber - reinforced composites with different degrees of "greenness" by mixing environmentally - friendly itaconic - acid - based epoxy resin (EIA) and bisphenol A diglycidyl ether (DGEBA). The main objectives of the research are: 1. **Improve the sustainability of materials**: By using bio - based materials (itaconic acid) to partially replace petroleum - based epoxy resins, reduce the dependence on fossil resources and environmental pollution. 2. **Improve the hygrothermal resistance and durability of materials**: Study the influence of different proportions of EIA and DGEBA mixtures on the hygrothermal resistance and mechanical properties of composites, in order to develop new bio - based epoxy resin composites with higher hygrothermal stability and durability. 3. **Optimize material properties**: Through experiments, compare the properties of composites with different degrees of "greenness" with those of traditional petroleum - based composites, and verify the feasibility and superiority of itaconic - acid - based epoxy resin in practical applications. ### Research background Epoxy resin (EP) is a thermosetting resin with excellent properties, chemical stability and electrical insulation properties, and is widely used in building materials, aerospace, coating adhesives and polymer - based composites and other fields. However, the wide application of epoxy resins and their composites has generated a large amount of waste, resulting in serious economic and environmental problems. Currently, the global epoxy resin production is expected to increase from 3.55 million tons in 2024 to 4.20 million tons in 2029, with a compound annual growth rate (CAGR) of 3.41%, among which bisphenol A (BPA) epoxy resin dominates. BPA epoxy resin will cause fossil pollution during the production process, and its use is restricted due to its biotoxicity. Therefore, there is an urgent need to develop environmentally - friendly green epoxy resins and their composites. Itaconic acid is an unsaturated dicarboxylic acid produced by fermenting carbohydrates such as glucose or starch, has a rich source and low cost, and is listed as one of the twelve most promising bio - based platform chemicals by the US Department of Energy. Itaconic - acid - based epoxy resin (EIA) has a high epoxy value and reactivity, but lacks rigid groups, which may lead to poor solvent resistance and heat resistance. In order to overcome these shortcomings, researchers propose to prepare carbon - fiber - reinforced composites with different degrees of "greenness" by mixing EIA and DGEBA to improve their hygrothermal stability and durability. ### Experimental methods 1. **Material preparation**: - Dicyandiamide (DICY) - Itaconic - acid - based epoxy resin (EIA) - Bisphenol A diglycidyl ether (DGEBA) - Epoxy resin (E - 20) - Urea (GLOC - 500) - Carbon fiber (T700) 2. **Preparation of cured epoxy resin**: - Add 20 wt% of E - 20 into a beaker and stir at high speed for 1 hour. - Add EIA and DGEBA in different proportions (0 wt%, 30 wt%, 40 wt%, 50 wt%) and continue to stir for 1 hour. - Add 8 wt% of DICY and 2 wt% of GLOC - 500, heat to 90 °C and stir at high speed for 30 minutes. - After vacuum degassing, pour it into a polytetrafluoroethylene mold and cure at a specific temperature and time. 3. **Preparation of carbon - fiber - composite laminates**: - Prepare 320 mm × 320 mm carbon - fiber - composite laminates in an autoclave. - Control the temperature and pressure during the curing process, with a final thickness of 2 mm and a total of 16 layers. 4. **Hygrothermal aging test**: - Conduct hygrothermal aging tests on laminates to observe the water absorption behavior and weight change of composites. - Measure the water absorption of samples according to ASTM D5229/D5229M standard. 5. **Characterization**: - Use Fourier - transform infrared spectroscopy (FTIR) to analyze the chemical structure changes of composites before and after hygrothermal aging. - Use Instron 3382 material testing machine to test the static mechanical properties of composites. - Use dynamic mechanical analyzer (DMA) and thermogravimetric analyzer (TGA) for dynamic thermal analysis and thermogravimetric analysis. - Use scanning electron microscope (SEM) to observe the composites.