Surface Constructions of Nano TiO_2 As the Environmental and Energy Materials

Changjian Lin

2007-01-01

Abstract:TiO_2 has attracted an increasing attention because of its variety of potential applications in environments and energies,such as gas sensing,self-cleaning,solar energy conversion, wettability and photo-catalysis applications.In this presentation,we summarize some progress in surface constructions of nano TiO_2 and its characterizations of physicochemistry and properties. (1)Superhydrophobic nanostructure TiO_2 films Superhydrophobic nanotube,nanopore and sponge-like structure TiO_2 films are fabricated by electrochemical method and self-assembled techniques.It is found that the adhesion of water droplet on these superhydrophobic nanostructure films are varied enormously from 5.0 to 75.6μN. It is clearly demonstrate that the strong adhesion is ascribed to capillary force and the capillarity induced negative pressure by the especial nanostructures between the solid/water interfaces.These results offered us a knowledge and opportunity to further understand the effect of structure on the wettability and adhesive force.It is expected that these TiO_2 nanostructure superhydrophobic films with distinct adhesion can be potentially used in many important industrial applications,such as self-cleaning,micropattern,liquid transportation and biocompatible implant materials etc. (2)Self-organized TiO_2 nanotube array and its photocatalytic activity Highly ordered TiO_2 nanotube arrays with a thick layer on titanium substrate are prepared in a new fluorined electrolyte containing glycerol and wider voltage range,from 5 to 33 V.The diameters of as-prepared TiO_2 nanotubes vary enormously from 20 to 150 nm and its thickness changes from a few hundreds nanometers to several micrometers.The photocatalytic activity of the nanotube arrays was evaluated by the degradation of methyl orange and phenol aqueous solution,respectively.The effects of some factors on its photocatalytic activity were investigated. The results show that the nanotube arrays have the higher photocatalytic activity in contrast to nanoparticle film prepared by sol-gel method. (3)Titanate nanotube films fabricated by layer-by-layer self-assembled technique The transparent titanate nanotubes films with a controllable thickness on glass or quartz substrate are prepared through layer-by-layer self-assembled technique.The film on glass substrate exhibits a light-induced super-hydrophilic property and it has a potential application as a new kind of self-clean glass.The photocatalytic activity of the titanate nanotube films were evaluated by the degradation of methyl orange and phenol in aqueous solution,respectively,and compared with that of the regular TiO_2 nanoparticle films prepared by sol-gel method under the identical conditions. (4)Nano TiO_2 composite coating and its dual functions of corrosion protection of metals TiO_2-SnO_2 composite films,sandwiched TiO_2/TiO_2-V_2O_5/TiO_2 and doped TiO_2 nanotubes composite films are constructed on the metallic surfaces.The anticorrosion property and the performance of photo-generated cathodic protection of the composite coatings are investigated. The all efforts have made in this work to solve three technical problems:(1)to increase the quantum efficiency of photoelectrochemical transferm;(2)to narrow the band gap of TiO_2 and to enhance the photoadsorption to illumination of visible light;(3)to last the life of h~+-e~- pair in the system and to enable a photogenerated cathodic protection to metallic substrates even in dark conditions.