Effect of Introducing Ce 3+ on the Emission Properties of Er 3+ /yb 3+ -Doped TeO 2 -WO 3 -Zno Glasses

Jiacheng Li,T. Xue,Yong Fan,Shunguang Li,Haoran Hu

2006-01-01

Abstract:Ce 3+ ions were introduced into the Er 3+ /Yb 3+ -codoped TeO 2 -WO 3 -ZnO glasses, and the effect of Ce 3+ on the emission properties at 1.5μm band and the upconversion luminescence of Er 3+ in the glasses was investigated. With the increasing of Ce 3+ concentration, the emission intensity of Er 3+ at 1.5μm band increases firstly, and then decreases. The optimal doping concentration of Ce 3+ is about 2.07×10 20 /cm 3 . As for the Er 3+ emission at 1.5-μm band, the fluorescence lifetime decreases a little from 3.4ms to 3.0ms, while the full width at half maximum (FWHM) hardly changes with the increase of Ce 3+ concentration. Due to the effective cross relaxation between Ce 3+ and Er 3+ : Er 3+ ( 4 I 11/2 )+Ce 3+ ( 2 F 5/2 )→Er 3+ ( 4 I 13/2 )+Ce 3+ ( 2 F 7/2 ), the upconversion emission intensity of Er 3+ is reduced greatly. But when Ce 3+ -doping concentration is too high, the other cross relaxation between Ce 3+ and Er 3+ : Er 3+ ( 4 I 13/2 )+Ce 3+ ( 2 F 5/2 )→Er 3+ ( 4 I 15/2 )+Ce 3+ ( 2 F 7/2 ) happens, which depopulates the 4 I 13/2 level of Er 3+ and results in the decrease of the emission intensity and fluorescence lifetime of Er 3+ at 1.5μm band.