Effect Of Size-Dependent Grain Structures On The Dynamics Of Nanoparticle Coalescence
Yiyang Zhang,Shuiqing Li,Wen Yan,Stephen D. Tse
DOI: https://doi.org/10.1063/1.4730773
IF: 2.877
2012-01-01
Journal of Applied Physics
Abstract:The effect of grain structure on the coalescence dynamics of anatase TiO2 nanoparticles at different temperatures is investigated using classical molecular dynamics (MD) simulation. Examination of local-lattice-orientation distributions reveals that the grain morphology of particles is highly dependent on size. For a single anatase nanoparticle below the melting temperature, an amorphous-to-crystalline transition occurs for diameters ranging from 2 to 2.5 nm as temperature increases. Below the transition diameter (for a given temperature), the entire nanoparticle is amorphous. Above the transition diameter, the nanoparticle consists of a crystalline core and an amorphous shell (4-6 angstrom). Considering that such grain-structure characteristics may lead to different dynamic behaviors, the coalescence between pairs of 2 nm-2 nm, 3 nm-3 nm, and 2 nm-3 nm nanoparticles is investigated. For 2 nm-2 nm nanoparticle coalescence, the process is independent of initial temperature and is seemingly viscosity-controlled with a dynamic temperature rise due to energy transfer from surface to internal kinetic (thermal). For 3 nm-3 nm nanoparticle coalescence, the process is sensitive to initial temperature. Above the melting temperature, the dynamics are similar to the 2 nm-2 nm amorphous case. Just below the melting point, coalescence consists of melting of the crystalline cores with subsequent large increase in temperature due to recrystallization. For 2 nm-3 nm nanoparticle coalescence, recrystallization of the 2 nm particle significantly increases the total temperature compared to the 2 nm-2 nm case. VC 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4730773]