Dressing Blood-Contacting Materials by a Stable Hydrogel Coating with Embedded Antimicrobial Peptides for Robust Antibacterial and Antithrombus Properties
Kunpeng Liu,Fanjun Zhang,Yuan Wei,Qinsheng Hu,Qingfeng Luo,Chong Chen,Jingyu Wang,Li Yang,Rifang Luo,Yunbing Wang
DOI: https://doi.org/10.1021/acsami.1c05167
2021-08-16
Abstract:Although dressing blood-contacting devices with robust and synergistic antibacterial and antithrombus properties has been explored for several decades, it still remains a great challenge. In order to endow materials with remarkable antibacterial and antithrombus abilities, a stable and antifouling hydrogel coating was developed via surface-initiated polymerization of sulfobetaine methacrylate and acrylic acid on a polymeric substrate followed by embedding of antimicrobial peptides (AMPs), including WR (sequence: WRWRWR-NH2) or Bac2A (sequence: RLARIVVIRVAR-NH2) AMPs. The chemical composition of the AMP-embedded hydrogel coating was determined through XPS, zeta potential, and SEM–EDS measurements. The AMP-embedded antifouling hydrogel coating showed not only good hemocompatibility but also excellent bactericidal and antiadhesion properties against Gram-positive and Gram-negative bacteria. Moreover, the hydrogel coating could protect the AMPs with long-term bioactivity and cover the positive charge of the dotted distributed AMPs, which in turn well retained the hemocompatibility and antifouling capacity of the bulk hydrogels. Furthermore, the microbiological results of animal experiments also verified the anti-infection performance in vivo. Histological and immunological data further indicated that the hydrogel coating had an excellent anti-inflammatory function. Therefore, the present study might provide a promising approach to prevent bacterial infections and thrombosis in clinical applications of blood-contacting devices and related implants.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c05167.Microphotograph of the sectional view of the hydrogel coating (Figure S1), SEM images of the cross section of the hydrogel coating (Figure S2), water absorption ability of PVC and hydrogel-coated samples (Figure S3), scratching test of the hydrogel coating using a steel tweezer (Figure S4), FTIR spectra of samples (Figure S5), map scanning of different hydrogel coatings in a section view by EDS (Figure S6), cell viability of HUVECs (Figure S7), E. coli and S. aureus colonies on agar plates from the samples (Figure S8), and XPS data of the coatings (Table S1) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology