Abstract:One of the current challenges in the development of flame retardants is the preparation of an environmentally friendly multi-element synergistic flame retardant to improve the flame retardancy, mechanical performance, and thermal performance of composites. This study synthesized an organic flame retardant (APH) using (3-aminopropyl) triethoxysilane (KH-550), 1,4-phthalaadehyde, 1,5-diaminonaphthalene, and 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) as raw materials, through the Kabachnik-Fields reaction. Adding APH to epoxy resin (EP) composites could greatly improve their flame retardancy. For instance, UL-94 with 4 wt% APH/EP reached the V-0 rating and had an LOI as high as 31.2%. Additionally, the peak heat release rate (PHRR), average heat release rate (AvHRR), total heat release (THR), and total smoke produced (TSP) of 4% APH/EP were 34.1%, 31.8%, 15.2%, and 38.4% lower than EP, respectively. The addition of APH improved the mechanical performance and thermal performance of the composites. After adding 1% APH, the impact strength increased by 15.0%, which was attributed to the good compatibility between APH and EP. The TG and DSC analyses revealed that the APH/EP composites that incorporated rigid naphthalene ring groups had higher glass transition temperatures (Tg) and a higher amount of char residue (C700). The pyrolysis products of APH/EP were systematically investigated, and the results revealed that flame retardancy of APH was realized by the condensed-phase mechanism. APH has good compatibility with EP, excellent thermal performance, enhanced mechanical performance and rational flame retardancy, and the combustion products of the as-prepared composites complied with the green and environmental protection standards which are also broadly applied in industry.

The Synergistic Effect of Biphenyl Structure and N Element in Flame Retardant and High Value-Added Recycling of Bio-Based Epoxy Resin

Synergistic Flame Retardancy Effect of Graphene Nanosheets and Traditional Retardants on Epoxy Resin

Flame retardant behavior of bio-based epoxy resin bearing pyridazinone and dynamic ester bond via self-blow-out and vesicular carbon formation

Design of epoxy resin with sustainability, high adhesion and excellent flame retardancy based on bio-based molecules

Fabrication of Flame-Retardant, Strong, and Tough Epoxy Resins by Solvent-Free Polymerization with Bioderived, Reactive Flame Retardant

An efficient flame retardant for epoxy resin: Preparation and pyrolytic behaviour

Advancing Flame Retardancy, Mechanical Properties, and Hydrophobicity of Epoxy Resins Through Bio-Based Cinnamaldehyde Derivative

Bio-derived modified halloysite nanotubes as eco-friendly flame retardants to endow epoxy with high thermal stability, mechanical performance and flame retardancy

Synergistic effects of aryl diazonium modified Few-Layer black Phosphorus/Ultrafine rare earth yttrium oxide with enhancing flame retardancy and catalytic smoke toxicity suppression of epoxy resin

Facile synthesis of a P/N-containing heterocyclic compound for simultaneous enhancement of heat resistance, mechanical properties and fire safety of epoxy resin

Preparation of Naphthalene-Based Flame Retardant for High Fire Safety and Smoke Suppression of Epoxy Resin

A novel P, N doped organic-inorganic hierarchical core-shell nanostructures: Reducing the fire risk of epoxy resin

Synthesis of Nitrogen‐rich Black Phosphorus Via a Diazotization Strategy for Efficient Flame Retardancy and Mechanical Properties of Epoxy Resins

Facile Synthesis of Intrinsically Flame‐retardant Epoxy Thermosets with High Mechanical Properties from Lignin Derivatives

Closed-Loop Recycling of Tough and Flame-Retardant Epoxy Resins

The synthesis of biphenyl ether/vanillin‐based flame retardants for enhancing both the flame retardant properties and mechanical performance of epoxy resin

P/N/Si‐containing synergistic flame retardants endowing lignin‐based epoxy resin with good flame retardancy, mechanical properties, and heat resistance

Facile construction of organic–inorganic hybrid flame-retardant system based on fully biomass: Improving the fire safety and mechanical property of epoxy resin

Bio-based flame retardants containing biphenyl structure for simultaneously enhancing mechanical properties and fire safety of epoxy resins

Flame retardancy, thermal behavior and mechanical properties of an epoxy resin and cyanate ester resin copolymer containing a bio phytate-based flame retardant

Combustion Behavior and Pyrolysis of Epoxy Resins Blended with Caged Bicyclic Dimelamine Phosphate