Spectral shifting and NIR down-conversion in Bi3+/Yb3+ co-doped Zn2GeO4

Guojun Gao,Mingying Peng,Lothar Wondraczek

DOI: https://doi.org/10.1039/c4tc01242a

2014-01-01

J. Mater. Chem. C

Abstract:We report on Zn2GeO4 co-doped with Yb3+ and Bi3+ as a model system for ultra-efficient down-conversion of the UV-A/blue part of the solar spectrum to the NIR.

What problem does this paper attempt to address?

Spectral shifting and NIR down-conversion in Bi 3+ /Yb 3+ co-doped Zn 2 GeO 4

guojun gao,mingying peng,lothar wondraczek

DOI: https://doi.org/10.1039/C4TC01242A

IF: 6.4

2014-01-01

Journal of Materials Chemistry C

Abstract:We report on spectral modification through NIR down-conversion (DC) photoluminescence (PL) in Yb3+-Bi3+-co-doped Zn2GeO4. Energetic downshifting (DS) of UV-A irradiation occurs via intrinsic luminescence of the high-bandgap semiconductor Zn2GeO4 as well as via active Bi3+ centres. In parallel, both species act as sensitizers for Yb3+, strongly extending its excitation region to similar to 500 nm. In the absence of Bi3+, band-to-band absorption of Zn2GeO4 in the UV region results in PL at similar to 475-625 nm. Doping with Yb3+ initiates energy transfer from trapped defect states to two neighbouring Yb3+ ions in a cooperative DC process, resulting in Yb3+-related photoemission at similar to 1000 nm. The introduction of Bi3+ into Zn2GeO4:Yb3+ greatly extends the absorption band to the visible blue region. Then, energy transfer also occurs through cooperative DC from Bi3+ to Yb3+. As a result, a strong increase in the absolute Yb3+-related PL intensity is observed. This enables ultra-efficient harvesting of UV-A to visible radiation for energy conversion processes.
Sensitized deep-ultraviolet up-conversion emissions of Gd 3+ via Tm 3+ and Yb 3+ in hexagonal NaYF 4 nanorods

Y. Y. Zhang,L. W. Yang,C. F. Xu,J. X. Zhong,C. Q. Sun

DOI: https://doi.org/10.1007/s00340-009-3827-y

2009-01-01

Applied Physics B

Abstract:Deep-ultraviolet (UV) up-conversion (UC) emissions in the region of 270∼330 nm of Gd 3+ under the excitation of a 980 nm laser diode in hexagonal Yb 3+ -Tm 3+ -Gd 3+ triply doped NaYF 4 nanorods synthesized using a hydrothermal method are reported. Spectral analyses indicate that the UV UC emissions originate from highly efficient energy transfer from Yb 3+ to Tm 3+ , then to Gd 3+ ions, and the intensity of the emission as well as the ratios of the emission peaks are strongly dependent on the doping concentrations and pump power. The materials are envisioned to have potential applications in anti-counterfeiting, optical and magnetic dual modal nanoprobes for biomedicine, solution-based scintillator materials and UV compact solid-state lasers.
Sensitized Deep-Ultraviolet Up-Conversion Emissions of Gd3+ Via Tm3+ and Yb3+ in Hexagonal NaYF4 Nanorods

Y. Y. Zhang,L. W. Yang,C. F. Xu,J. X. Zhong,C. Q. Sun

DOI: https://doi.org/10.1007/s00340-009-3827-y

2009-01-01

Abstract:Deep-ultraviolet (UV) up-conversion (UC) emissions in the region of 270 similar to 330 nm of Gd3+ under the excitation of a 980 nm laser diode in hexagonal Yb3+-Tm3+-Gd3+ triply doped NaYF4 nanorods synthesized using a hydrothermal method are reported. Spectral analyses indicate that the UV UC emissions originate from highly efficient energy transfer from Yb3+ to Tm3+, then to Gd(3+)ions, and the intensity of the emission as well as the ratios of the emission peaks are strongly dependent on the doping concentrations and pump power. The materials are envisioned to have potential applications in anti-counterfeiting, optical and magnetic dual modal nanoprobes for biomedicine, solution-based scintillator materials and UV compact solid-state lasers.
Near-Infrared Down-Conversion In Rare-Earth-Doped Chloro-Sulfide Glass Ges2-Ga2s3-Cscl: Er, Yb

Bo Fan,Céline Point,Jean Luc Adam,Xianghua Zhang,Xianping Fan,Hongli Ma

DOI: https://doi.org/10.1063/1.3665638

IF: 2.877

2011-01-01

Journal of Applied Physics

Abstract:Chloro-sulfide glass with low phonon energy, GeS2-Ga2S3-CsCl, is co-doped with Er and Yb. This active glass is a potential downconversion material for modifying the solar spectrum to improve the efficiency of solar cells. Two downconversion processes from visible to near infrared are observed. In the first process, an energy transfer between Er3+ ions and Yb3+ ions occurs. In that case, one photon is absorbed by the I-4(15/2) -> H-2(11/2) (Er3+) transition and then two photons are emitted by F-2(5/2) -> F-2(7/2) (Yb3+) and I-4(13/2) -> I-4(15/2) (Er3+), respectively. In the second process, downconversion takes place from the charge-transfer state of Yb3+-S2- to the 4f states of Yb3+ ions, which leads to an intense excitation band between 400 nm and 600 nm, and an emission at 1000 nm. Quantum yields for downconversion are measured. The highest quantum yields of emission below 1200 nm and 1650 nm are equal to 51% and 76%, respectively. (C) 2011 American Institute of Physics. [doi: 10.1063/1.3665638]
Enhanced energy transfer and near-infrared luminescence by crystal field regulation in Zn3Ga2GeO8: Cr3+, Yb3+

Jian Yang,Chenglong Xie,Lei Zhao

DOI: https://doi.org/10.1039/d4dt02243b

IF: 4

2024-09-19

Dalton Transactions

Abstract:Near-infrared (NIR)-emitting phosphors with broadband absorption from ultraviolet to visible light have been considered significant spectral convert materials for solar cells. In this work, the NIR phosphors Zn3Ga2GeO8 (ZGGO): Cr3+, Yb3+ spinel solid solution were synthesized by classical high-temperature solid-state method. With increased of the doping concentration of the Cr3+ ions in ZGGO: Cr3+, Yb3+, more distorted octahedron appears around Cr3+ ions, which can be increased the crystal field splitting. This process was accompanied by a broadening of the NIR emission from Cr3+ 4T2→4A2 transition, and enlarge the overlap area between the absorption spectrum of Yb3+ and the emission spectrum of Cr3+, which resulting in efficient energy transfer occurred between Cr3+ and Yb3+. In the case of high-concentration doping of Cr3+, the near-infrared luminescence intensity of Yb3+ was more than 8 times that of low-concentration doped Cr3+. There is reason to believe that Cr3+, Yb3+ co-doped ZGGO phosphor is a potential spectral converter for silicon-based solar cells, thereby improving photovoltaic conversion efficiency.

chemistry, inorganic & nuclear
Near-infrared Emission of Yb3+ Through Energy Transfer from ZnO to Yb3+ in Glass Ceramic Containing ZnO Nanocrystals.

Qun Luo,Xvsheng Qiao,Xianping Fan,Xianghua Zhang

DOI: https://doi.org/10.1364/ol.36.002767

2011-01-01

Abstract:Yb(3+)-doped glass and glass ceramic containing ZnO nanocrystals were prepared by the melting-quenching method and subsequent heat treatment. Intense near-IR emission around 1000 nm that originated from the transition of Yb(3+):(2)F(5/2)→(2)F(7/2) was generated as a result of energy transfer from oxygen interstitials in ZnO nanocrystals to Yb(3+) with energy transfer efficiency of about 10%. The quantum yield for the near-IR emission of Yb(3+) under the excitation of 390 nm was about 16.7%. These materials have potential application in achieving high-efficiency Si solar cells via spectrum modification.
Enhanced NIR Down-Conversion of Yb3+ in Fluorosilicate Glass-Ceramics Co-Doped with Bi Ions

Bin Yang,Huidan Zeng,Yanyan Zhang,Yifan Deng,Yangyang Guo,Jianding Chen,Guorong Chen

DOI: https://doi.org/10.1016/j.optmat.2018.04.001

IF: 3.754

2018-01-01

Optical Materials

Abstract:The fluorescence properties of Bi3+/Yb3+ co-doped SiO2-Al2O3-P2O5-YF3 glasses and glass-ceramics are investigated. The 6s(2)-type Bi3+ is used as a novel sensitizer for near infrared (NIR) down-conversion (DC) of Yb3+ ions due to its allowed excitations favorable to the high absorption of excited energy. Involvement of the energy transfer (ET) process from Bi3+ to Yb3+ under the ultraviolet (UV) excitation is demonstrated for all Bi3+/Yb3+ co-doped glass sample's. Based on crystallization kinetics analysis, thermal treatment is performed on glass samples under different heating conditions to induce homogeneous nucleation and crystal growth. Emission and excitation spectra as well as Bi3+ emission decay curves confirm that the ET from Bi3+ to Yb3+ is tremendously intensified due to proper crystallization treatment. The possible ET mechanism is discussed with the help of the simplified energy level diagrams of Bi3+ and Yb3+. The present Bi3+/Yb3+ co-doped glass ceramics are likely applied to solar cells via spectrum conversion.
Broadband Downconversion of Ultraviolet Light to Near‐Infrared Emission in Bi3+–Yb3+‐Codoped Y2O3 Phosphors

Xiao Yong Huang,Xiao Hong Ji,Qin Yuan Zhang

DOI: https://doi.org/10.1111/j.1551-2916.2010.04184.x

IF: 4.186

2010-01-01

Journal of the American Ceramic Society

Abstract:The metal ion Bi3+ has been shown to be an efficient broadband sensitizer for Yb3+ ion in the Y2O3 host lattice. Upon ultraviolet‐light excitation in the allowed 1S0→3P1 transition of Bi3+ ions, the characteristic near infrared luminescence of Yb3+ ions due to the 2F5/2→2F7/2 transition was observed as a result of energy transfer from Bi3+ to Yb3+ ions. It demonstrates that cooperative downconversion can be realized for Bi3+–Yb3+ coupling. Yb3+‐concentration‐dependent quantum efficiency was evaluated and the maximum efficiency reached 173.8%. These phosphors are promising for the enhancement of energy efficiency of crystalline Si solar cells via spectrum shifting.
Quantum Cutting Downconversion by Cooperative Energy Transfer from Bi 3+ to Yb 3+ in Y 2 O 3 Phosphor

Wei Xian-Tao,Zhao Jiang-Bo,Chen Yong-Hu,Yin Min,Li Yong

DOI: https://doi.org/10.1088/1674-1056/19/7/077804

2010-01-01

Chinese Physics B

Abstract:Bi3+ and Yb3+ codoped cubic Y2O3 phosphors are prepared by pechini sol-gel method. Strong near-infrared (NIR) emission around 980 nm from Yb3+ (F-2(5/2) ->(2) F-7/2) is observed under ultraviolet light excitation. A broad excitation band ranging from 320 to 360 rim, owing to the 6s(2) -> 6s6p transition of Bi3+ ions, is recorded when the Yb3+ emission is monitored, which suggests a very efficient energy transfer from Bi3+ ions to Yb3+ ions. The Yb3+ concentration dependences of both the Bi3+ and the Yb3+ emissions are investigated. The decay curve of Bi3+ emission under the excitation of 355 nm pulse laser is used to explore the Bi3+ -> Yb3+ energy transfer process. Cooperative energy transfer (CET) is discussed as a possible mechanism for the near-infrared emission.
Yb^3+-doped GeS_2-Ga_2S_3-CsCl Glass with Broad and Adjustable Absorption/excitation Band for Near-Infrared Luminescence

Bo Fan,Bai Xue,Xianghua Zhang,Jean-Luc Adam,Xianping Fan

DOI: https://doi.org/10.1364/ol.38.002280

2013-01-01

Abstract:The luminescent property of Yb(3+) ions in GeS(2)-Ga(2)S(3)-CsCl glasses with different CsCl contents has been studied. All the samples demonstrate a broad excitation band in the UV or/and visible range, depending on the composition, which is attributed to the charge transfer of the Yb(3+)-S(2-)/Cl(-) couple. The width of the excitation/absorption band can be as large as 150 nm. Moreover, with the increase of CsCl content, the peak position of the band can be continuously adjusted from 458 to 380 nm, due to the increase of the local average electronegativity around Yb(3+) ions. The broad and adjustable excitation band makes the Yb(3+)doped GeS(2)-Ga(2)S(3)-CsCl glass interesting for modifying the solar spectrum by absorbing strongly in the UV/blue region for emission around 1 μm. This kind of material is the key to adapting the solar spectrum to the response of silicon photovoltaic solar cells.
Broadband Downconversion In Bi3+, Yb3+-Co-Doped Yvo4 Phosphor

Gui Cheng Jiang,Xiantao Wei,Yonghu Chen,Min Yin

DOI: https://doi.org/10.1166/jnn.2011.5231

2011-01-01

Journal of Nanoscience and Nanotechnology

Abstract:Yttrium vanadate phosphors co-doped with Bi3+ and Yb3+ ions have been prepared via the solid-state reaction. The phosphors were characterized by various methods including X-ray diffraction, photoluminescence excitation and photoluminescence spectra. Upon ultraviolet (UV) light excitation, an intense near-infrared (NIR) emission of Yb3+ corresponding to the transition of F-2(5/2) > F-2(7/2) peaking at 985 nm was observed as a result of energy transfer from O2--V5+ or Bi3+-V5+ charge transfer state (CTS) to Yb3+. A broad excitation band ranging from 250 to 375 nm was recorded when the Yb3+ emission was monitored, which suggests an efficient energy transfer from CTS to Yb3+ ions. The dependence of Yb3+ doping concentration on the visible emission, the NIR emission and decay lifetime has been investigated. The results of visible and NIR spectral evolution with temperature indicate that the mechanism for the NIR-emission is mainly phonon-assisted energy transfer at room temperature, while the mechanism is mainly cooperative energy transfer at low temperature. The YVO4:Bi3+, Yb3+ phosphor has prospects for realizing high efficiency crystalline Si solar cells by converting broadband UV energy into NIR light.
Broadband Spectral Modification from Visible Light to Near-Infrared Radiation Using Ce3+-Er3+ Codoped Yttrium Aluminium Garnet

Jiajia Zhou,Yu Teng,Xiaofeng Liu,Song Ye,Zhijun Ma,Jianrong Qiu

DOI: https://doi.org/10.1039/c0cp00204f

2010-01-01

Abstract:Broadband spectral conversion from visible light to near-infrared radiation in Ce(3+)-Er(3+) codoped yttrium aluminium garnet is reported. Excitation, emission, time-resolved luminescence spectra and fluorescence decay curves have been measured to prove the energy transfer from Ce(3+) to Er(3+). The broadband and strong absorption of Ce(3+), efficient energy transfer from Ce(3+) to Er(3+), and three-photon quantum cutting process in Er(3+) ions result in efficient near-infrared emission when excited by 400-500 nm broad visible light. The energy of the Er(3+) ((4)I(13/2)→(4)I(15/2)) transition matches well with the band gap of germanium (Eg ∼ 0.785 eV). Ce(3+)-Er(3+) codoped yttrium aluminium garnet is promising for the enhancement of conversion efficiency of germanium solar cells.
Broadband Spectral Conversion of Visible Light to Near-Infrared Emission Via Energy Transfer from Ce3+ to Nd3+/Yb3+ in YAG

Zhou Jiajia,Teng Yu,Liu Xiaofeng,Ma Zhijun,South China University of Technology

DOI: https://doi.org/10.1557/jmr.2010.84

2011-01-01

Abstract:Broadband spectral conversion from visible light to near-infrared radiation in Ce3+–Nd3+/Yb3+ codoped yttrium aluminum garnet is reported. Excitation, emission spectra, and decay curves have been measured to prove the energy transfer from Ce3+ to Nd3+ or Yb3+. The energy transfer efficiencies have been estimated, and the mechanisms of the energy transfer between Ce3+ and Nd3+/Yb3+ have been proposed. Ce3+–Nd3+ codoped YAG can obtain more effective emission in the desired near-infrared region (around 1100 nm) through broadband conversion, showing potential application to improve the conversion efficiency of Si solar cells.
NIR light guided enhanced photoluminescence and temperature sensing in Ho3+/Yb3+/Bi3+ co-doped ZnGa2O4 phosphor

Monika,Ram Sagar Yadav,Anita Rai,Shyam Bahadur Rai

DOI: https://doi.org/10.1038/s41598-021-83644-9

IF: 4.6

2021-02-18

Scientific Reports

Abstract:Abstract The conversion of NIR light into visible light has been studied in Ho 3+ /Yb 3+ /Bi 3+ co-doped ZnGa 2 O 4 phosphor for the first time. The crystallinity and particles size of the phosphor increase through Bi 3+ doping. The absorption characteristics of Ho 3+ , Yb 3+ and Bi 3+ ions are identified by the UV–vis-NIR measurements. The Ho 3+ doped phosphor produces intense green upconversion (UC) emission under 980 nm excitations. The emission intensity ~ excitation power density plots show contribution of two photons for the UC emissions. The UC intensity of green emission is weak in the Ho 3+ doped phosphor, which enhances upto 128 and 228 times through co-doping of Yb 3+ and Yb 3+ /Bi 3+ ions, respectively. The relative and absolute temperature sensing sensitivities of Ho 3+ /Yb 3+ /5Bi 3+ co-doped ZnGa 2 O 4 phosphor are calculated to be 13.6 × 10 −4 and 14.3 × 10 −4 K −1 , respectively. The variation in concentration of Bi 3+ ion and power density produces excellent color tunability from green to red via yellow regions. The CCT also varies with concentration of Bi 3+ ion and power density from cool to warm light. The color purity of phosphor is achieved to 98.6% through Bi 3+ doping. Therefore, the Ho 3+ /Yb 3+ /Bi 3+ :ZnGa 2 O 4 phosphors can be suitable for UC-based color tunable devices, green light emitting diodes and temperature sensing.

multidisciplinary sciences
Ultrabroad NIR luminescence and energy transfer in Bi and Er/Bi co-doped germanate glasses.

Mingying Peng,Na Zhang,Lothar Wondraczek,Jianrong Qiu,Zhongmin Yang,Qinyuan Zhang

DOI: https://doi.org/10.1364/OE.19.020799

IF: 3.8

2011-01-01

Optics Express

Abstract:The effects of temperature, pump power and excitation wavelength on near-infrared photoluminescence from Bi-doped multi-component germanate glasses are presented. Compared to conventional silica/silicate matrices, the examined material exhibits superior resistance to thermal quenching and less pronounced excited state absorption for pumping at 808 nm. It is shown that by selecting the optimal excitation wavelength, photoemission can be initiated from multiple active centers in parallel, resulting in an emission bandwidth (full width at half maximum) of more than 370 nm. Er3+/Bi co-doping is presented as an effective means to significantly enhance emission intensity around 1.5 mu m by suppressing the typical Er3+-related red-to-green upconversion. Besides its relevance for Bi-doped materials, this also indicates a new route towards improving the performance of Er-based optical devices. The mechanism of Er3+-> Bi energy transfer is examined in detail. Adjusting the molar ratio between both species provides an effective tool for tuning the emission scheme and further increasing emission bandwidth. (C) 2011 Optical Society of America
NIR Downconversion and Energy Transfer Mechanisms in Tb3+/Yb3+ Codoped Na5Lu9F32 Single Crystals.

Jianxu Hu,Yuanpeng Zhang,Haiping Xia,Huanqing Ye,Baojiu Chen,Yongsheng Zhu

DOI: https://doi.org/10.1021/acs.inorgchem.8b00867

IF: 4.6

2018-01-01

Inorganic Chemistry

Abstract:Tb3+/Yb3+ codoped Na5Lu9F32 single crystals with near-infrared (NIR) emission are achieved by an improved Bridgman approach. Energy transfer from Tb3+ to Yb3+ ions is affirmed by the photoluminescence (PL) emission spectra and decay curves characterization. On the basis of the analysis of energy transfer rate dependence on the Yb3+ concentration, the interaction between Tb3+ and Yb3+ ions in Na5Lu9F32 single crystals is confirmed through the one-to-one energy transfer process. Results demonstrate that the prepared Na5Lu9F32 single crystals might be promising candidates to convert sunlight to improve the performance of the silicon solar cells.
Broadband Downconversion from Oxygen-Deficient Centers to Yb3+ in Germanate Glasses

Yixi Zhuang,Yu Teng,Jiajia Zhou,Song Ye,Xiaofeng Liu,Geng Lin,Jian Ruan,Jianrong Qiu

DOI: https://doi.org/10.1364/josab.26.002185

2009-01-01

Abstract:We report broadband downconversion from ultraviolet to near-infrared in Yb3+-doped oxygen-deficient SrO-Al2O3-GeO2 glasses. Oxygen-deficient centers are introduced in germanate glasses by adding metal Al instead of corresponding oxide (Al2O3). Tunable luminescence related to these defects is observed. Conversion of broadband ultraviolet light to blue-green tunable luminescence and to near-infrared emission is detected in glasses. The energy transfer efficiency increases with increasing Yb2O3 concentration. The dependence of energy transfer efficiency on wavelength is also discussed. (C) 2009 Optical Society of America
Ultraviolet to near-infrared downconversion in Yb 3+-doped Sr 2CeO 4

Ru Zhou,Xiantao Wei,Yonghu CHEN,Changkui DUAN,Min YIN

DOI: https://doi.org/10.1002/pssb.201147431

2012-01-01

Abstract:Efficient bluegreen emission is observed for Sr2CeO4 under ultraviolet excitation ranging from 250 to 400?nm and this is ascribed to the emission of the O2-Ce4+ charge transfer (CT) states. Under the excitation of ultraviolet light in the broad absorption band, an intense near-infrared (NIR) emission of Yb3+: 2F5/2???2F7/2 around 1 mu m is observed for Yb3+-doped Sr2CeO4. The Yb3+ concentration-dependent luminescence properties and the lifetimes of both the visible CT emission and the NIR Yb3+ emission are investigated under the excitation of a 266-nm pulsed laser beam. The fast decline of the lifetimes of the CT emission with the increasing Yb3+ concentration suggests efficient energy transfer from the host to Yb3+ ions. A cooperative energy transfer (CET) mechanism is proposed to explain the NIR downconversion process. The Sr2CeO4:Yb3+ phosphors can convert ultraviolet photons into NIR photons around 1 mu m with a twofold increase in the photon number via CET, which has potential application in enhancing the photovoltaic conversion efficiency of silicon-based solar cells.
Tunable Ultraviolet/visible to Near-Infrared Down-Conversion Luminescence in the Er3+, Yb3+ Co-Doped (y0.88la0.09zr0.03)2o3 Transparent Ceramics

Yue Hu,Muhammad Shahid,Wei Pan

DOI: https://doi.org/10.1016/j.optmat.2017.05.030

IF: 3.754

2017-01-01

Optical Materials

Abstract:Herein, we report an efficient ultraviolet/visible to near-infrared (NIR) down-conversion luminescence phenomenon in transparent Er3+, Yb3+ co-doped (Y0.88La0.09Zr0.03)(2)O-3 ceramics. Almost fully densified (Y0.88La0.09Zr0.03)(2)O-3 transparent ceramic has been prepared by vacuum sintering at 1800 degrees C with different contents of Er3+ and Yb3+ elements. The intensity ratio of Yb3+: F-2(5/2) -> F-2(7/2) emission (similar to 1000 nm) to the Er3+: 4I(13/2) -> I-4(15/2) emission (similar to 1550 nm) has been tuned by adjusting the excitation wavelength. Phonon-assist quantum cutting from the (4)G(11/2) level of Er3+ with two energy transfer (ET) processes to Yb3+ has been determined, which enhances the Yb3+ emission around the wavelength of 1000 nm. It is found that when one photon around 379 nm is absorbed, two photons around 1000 nm will be emitted, and hence the quantum efficiency is estimated to be similar to 182% in this transparent ceramics. The mechanism of the visible to near-infrared (NIR) down-conversion luminescence in the Er3+, Yb3+ co-doped (Y0.88La0.09Zr0.03)(2)O-3 ceramics has been discussed. (C) 2017 Elsevier B.V. All rights reserved.
Broadband Conversion of Ultraviolet to Visible and Near-Infrared Emission in Gd3+/Yb3+ Codoped Germanate Glass

Lili Tao,Bo Zhou,Gongxun Bai,Yonggang Wang,Jianhua Hao,Yuen H. Tsang

DOI: https://doi.org/10.1016/j.jnoncrysol.2013.04.056

IF: 4.458

2013-01-01

Journal of Non-Crystalline Solids

Abstract:Gd3+/Yb3+ co-doped germanate glasses were fabricated using the melt-quenching method. Broadband visible emission was observed from the gadolinium doped germanate glasses under ultraviolet (UV) excitation, and white-light was obtained by modifying Yb3+ co-dopant concentration. Through this co-doped system, the white-light emission can be further converted into the near-infrared range which is matched well with the energy band gap of commercial silicon solar cell. The possible energy transfer processes involved are proposed and discussed according to the excitation, emission and fluorescence decay measurements. The effect of Yb3+ ion concentration with respect to fixed Gd3+ ions on the visible and near-infrared (NIR) emission has also been studied. The conversion efficiency from visible to near-infrared is as high as 69.3% in the GZN: 0.2Gd2O3–0.6Yb2O3 sample. The results indicate that this material is potential in various applications, such as white LED, enhancing silicon solar cell efficiency, and so on.

Spectral shifting and NIR down-conversion in Bi<sup>3+</sup>/Yb<sup>3+</sup> co-doped Zn<sub>2</sub>GeO<sub>4</sub>

Spectral shifting and NIR down-conversion in Bi 3+ /Yb 3+ co-doped Zn 2 GeO 4

Sensitized deep-ultraviolet up-conversion emissions of Gd 3+ via Tm 3+ and Yb 3+ in hexagonal NaYF 4 nanorods

Sensitized Deep-Ultraviolet Up-Conversion Emissions of Gd3+ Via Tm3+ and Yb3+ in Hexagonal NaYF4 Nanorods

Near-Infrared Down-Conversion In Rare-Earth-Doped Chloro-Sulfide Glass Ges2-Ga2s3-Cscl: Er, Yb

Enhanced energy transfer and near-infrared luminescence by crystal field regulation in Zn3Ga2GeO8: Cr3+, Yb3+

Near-infrared Emission of Yb3+ Through Energy Transfer from ZnO to Yb3+ in Glass Ceramic Containing ZnO Nanocrystals.

Enhanced NIR Down-Conversion of Yb3+ in Fluorosilicate Glass-Ceramics Co-Doped with Bi Ions

Broadband Downconversion of Ultraviolet Light to Near‐Infrared Emission in Bi3+–Yb3+‐Codoped Y2O3 Phosphors

Quantum Cutting Downconversion by Cooperative Energy Transfer from Bi 3+ to Yb 3+ in Y 2 O 3 Phosphor

Yb^3+-doped GeS_2-Ga_2S_3-CsCl Glass with Broad and Adjustable Absorption/excitation Band for Near-Infrared Luminescence

Broadband Downconversion In Bi3+, Yb3+-Co-Doped Yvo4 Phosphor

Broadband Spectral Modification from Visible Light to Near-Infrared Radiation Using Ce3+-Er3+ Codoped Yttrium Aluminium Garnet

Broadband Spectral Conversion of Visible Light to Near-Infrared Emission Via Energy Transfer from Ce3+ to Nd3+/Yb3+ in YAG

NIR light guided enhanced photoluminescence and temperature sensing in Ho3+/Yb3+/Bi3+ co-doped ZnGa2O4 phosphor

Ultrabroad NIR luminescence and energy transfer in Bi and Er/Bi co-doped germanate glasses.

NIR Downconversion and Energy Transfer Mechanisms in Tb3+/Yb3+ Codoped Na5Lu9F32 Single Crystals.

Broadband Downconversion from Oxygen-Deficient Centers to Yb3+ in Germanate Glasses

Ultraviolet to near-infrared downconversion in Yb 3+-doped Sr 2CeO 4

Tunable Ultraviolet/visible to Near-Infrared Down-Conversion Luminescence in the Er3+, Yb3+ Co-Doped (y0.88la0.09zr0.03)2o3 Transparent Ceramics

Broadband Conversion of Ultraviolet to Visible and Near-Infrared Emission in Gd3+/Yb3+ Codoped Germanate Glass