Hot deformation behavior and resultant microstructural evolution of dilute Mg–Bi–Sn–Mn alloy during hot compression
Guo-lei Liu,Zhi-yong You,Wei-li Cheng,Lin Luo,Hui Yu,Li-fei Wang,Hang Li,Ze-qin Cui,Jin-hui Wang
DOI: https://doi.org/10.1016/j.jmrt.2023.08.093
IF: 6.267
2023-08-23
Journal of Materials Research and Technology
Abstract:This study investigated the dynamic recrystallization (DRX) mechanism and hot-deformation behavior of the solution-treated Mg-0.5Bi-0.5Sn-0.5Mn (BTM000) alloy during hot compression at temperatures ranging from 175 to 225 °C with a strain rate of 0.001–1 s −1 . Processing maps and constitutive equation were used for a detailed analysis. The results showed a strong correlation with a coefficient of 0.987669, indicating the accuracy of proposed method in predicting the hot deformation behavior. The average activation energy ( Q ) was found to be 139.10 kJ/mol, and the stress component ( n) was calculated to be 7.96, suggesting that cross-slip is the primary deformation mechanism. Based on the processing maps, the most suitable processing conditions were found to be within the range of 210–290 °C with a strain rate of 0.37–1 s −1 . At a low strain rate of 0.001 s −1 , the dominant deformation mechanism observed was pyramidal slip. However, at higher temperatures (175–325 °C) and a strain rate of 1 s −1 , a transformation from basal slip to a combination of basal slip and pyramidal slip was observed. Under low-temperature and low-strain-rate conditions (175 °C/0.001 s −1 ), continuous dynamic recrystallization (CDRX) was the dominant mechanism. In contrast, under other deformation conditions (175 °C/1 s −1 , 325 °C/0.001 s −1 , 325 °C/1 s −1 ), a synergistic effect between discontinuous dynamic recrystallization (DDRX) and CDRX was evident. Through quasi-situ kernel average misorientation (KAM) characterization, it was observed that the local storage energy associated with CDRX was significantly lower compared to the combination of CDRX and DDRX, indicating a higher likelihood of CDRX occurrence.
materials science, multidisciplinary,metallurgy & metallurgical engineering