Abstract:The relatively low hydrothermal stability of Al-rich Cu-SSZ-13 catalysts hinders their practical application in ammonia selective catalytic reduction (NH3-SCR) reaction. Rare-earth ions were introduced into the Al-rich SSZ-13 zeolite using an organotemplate-free synthesis prior to the exchange of Cu2+ ions. Among the rare-earth ions tested (Ce, La, Sm, Y, Yb), Y shows significant enhancement of the hydrothermal stability and NH3-SCR activities after severe hydrothermal aging at 800 degrees C for 16 h when compared with Cu-SSZ-13 without Y. Cu-Y-SSZ-13 catalysts with various amounts of Y were prepared, and it is found that with increasing Y content, the low temperature NO conversions can be improved even after hydrothermal aging. SEM-EDX analysis together with two-dimensional multiple quantum magic-angle-spinning nuclear magnetic resonance (Na-23 MQ MAS NMR) confirms that the Y ions are successfully incorporated into the ion-exchange sites of the SSZ-13 zeolite. Results from Al-27 MAS, Si-29 MAS NMR, temperature-programmed desorption of ammonia (NH3-TPD) and quantitative H-1 MAS NMR indicate that Y can stabilize the framework Al and also preserve the BrOnsted acid sites in the Al-rich SSZ-13 zeolite. The hydrogen temperature programmed reduction (H-2-TPR), ultraviolet-visible-near infrared spectroscopy (UV-vis-NIR) and diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) of nitric oxide (NO) or NH3 adsorption demonstrate that introduction of Y ions causes Cu2+ ions to preferentially occupy the 6-MR, which has high hydrothermal stability. However, too much of Y may lead to activity loss at both low and high temperatures. The optimized Al-rich Cu-Y-SSZ-13 with 2.8 wt% of copper (Cu) and 1.3 wt% of Y displays almost the same deNO(x) activities as the conventional organotemplated high silica Cu-SSZ-13 catalyst in a wide reaction temperature window of 150-650 degrees C after severe hydrothermal treatment. Rare-earth ions could be an effective additive for Cu-SSZ-13 catalysts to further improve their hydrothermal stability for practical applications.

Direct Synthesis of High Silica Ssz-16 Zeolite with Extraordinarily Superior Performance in Nh3-Scr Reaction

Direct Synthesis of SSZ-13 Zeolite Using Tetraethylammonium Hydroxide As an Efficient Organic Template in the Presence of Conventional Aluminum and Silicon Sources

Facile Synthesis of SSZ-16 Nanoaggregates with Excellent Performance in NH3-SCR Reaction

One-Pot Synthesis of Ce-SSZ-39 Zeolite with Performance in the NH3-SCR Reaction

Cu-SSZ-13 zeolite–metal oxide hybrid catalysts with enhanced SO2-tolerance in the NH3-SCR of NOx

TEAOH-assisted Cost-Effective Preparation of SSZ-13 Using L Zeolite As Al Source

Potassium-directed sustainable synthesis of new high silica small-pore zeolite with KFI structure (ZJM-7) as an efficient catalyst for NH3-SCR reaction

Synthesis Of Ssz-13 Zeolite With High Molar Ratio Of Sio2 To Al2o3 By Crystal Transformation Method Using Tetraethyl Ammonium Hydroxide As Template

Enhanced hydrothermal stability of Cu-SSZ-13 by compositing with Cu-SAPO-34 in selective catalytic reduction of nitrogen oxides with ammonia

Rare-earth ion exchanged Cu-SSZ-13 zeolite from organotemplate-free synthesis with enhanced hydrothermal stability in NH3-SCR of NOx

Spotlight on Cu/SAPO-34 with high hydrothermal stability induced by a small amount of SSZ-39

Rapid synthesis and hydrothermal stability enhancement of Cu-SSZ-13 zeolites for nitrogen oxide removal

Economical and Sustainable Synthesis of Small-Pore Chabazite Catalysts for NOx Abatement by Recycling Organic Structure- Directing Agents

Solvent-free synthesis of aluminosilicate SSZ-39 zeolite

Insight into solid-state ion-exchanged Cu-based zeolite (SSZ-13, SAPO-18, and SAPO-34) catalysts for the NH3-SCR reaction: The promoting role of NH4-form zeolite substrates

Environmental benign synthesis of Nano-SSZ-13 via FAU trans-crystallization: Enhanced NH3-SCR performance on Cu-SSZ-13 with nano-size effect

Hard Template-Assisted Trans-Crystallization Synthesis of Hierarchically Porous Cu-SSZ-13 with Enhanced NH3-SCR Performance

Cu-OFF/ERI zeolite: Intergrowth structure synergistically boosting NH3-SCR performance

Cu-exchanged Al-rich SSZ-13 zeolite from organotemplate-free synthesis as NH3-SCR catalyst: Effects of Na+ ions on the activity and hydrothermal stability

Preparation of SSZ-13 zeolites and their NH 3 -selective catalytic reduction activity

Cu-OFF/ERI Zeolite: Intergrowth Structure Synergistically Boosting Selective Catalytic Reduction of NOx with NH3