Microstructure and Properties of Mo-Si-B-Y2O3 Composite Coating on Nickel-Based Alloy by Laser Cladding

Zican Ding,Ziyu Fang,Guangyuang Wang,Chengcheng Wu,Sen Yang

DOI: https://doi.org/10.1016/j.optlastec.2023.109473

2023-01-01

Abstract:A Mo-12Si-8.5B-Y2O3 composite coating was prepared on the surface of nickel-based alloy by laser cladding. In this study, the effect of Y2O3 on the coating structure and properties is examined. Macroscopic morphology, microstructure, and phase structure of the coatings were examined by optical microscopy (OM), scanning electron microscopy (SEM), energy spectrometry (EDS), and X-ray diffraction (XRD). The wear resistance and high-temperature oxidation resistance of the coatings were evaluated using a high-temperature tribometer and a simultaneous thermal analyzer. The experimental results indicate that the microhardness and high-temperature oxidation resistance of the coating increased with an increase in Y2O3 content. However, excessive Y2O3 contributed to an increased cracking tendency of the coating and a decrease in high-temperature frictional wear resistance. The composite coating containing 1 wt.% Y2O3 was of the best quality. The corresponding clad layer contained a mixture of alpha-Mo + Mo5SiB2 (T2) + Mo3Si phases with a microhardness value of 931 HV0.5, which was 5.6 times the substrate value. The Y2O3-modified coating reached a stable state after extended oxidation at 900 degrees C with less mass loss. The composite coating improved the high-temperature oxidation resistance of the substrate.