Abstract:Three thin films (DLC, a-C, and TiN) were performed on Ti6Al4V by chemical vapor deposition. Carbon ion implantation was pretreated for DLC and a-C films while Ti transition layer was pretreated for TiN film to strengthen the bonding strength. X-ray diffraction, Raman measurement, nano-hardness and nano-scratch tester, and cross-section etching by FIB method were used to analyze film characteristics. Tribological behaviors of these coatings were studied by articulation with both ZrO 2 and UHMWPE balls using ball-on-disk sliding. The thickness values reached ~0.46, ~0.33, and ~1.67 μm for DLC, a-C, and TiN film, respectively. Nano-hardness of the coatings compared with that of untreated and bonding strength (critical load in nano-scratch test) values of composite coatings compared with that of monolayer film all increased significantly, respectively. Under destructive test (ZrO 2 ball conterface) in bovine serum lubrication, TiN coating revealed the best wear resistance while DLC showed the worst. Film failure was mainly attributed to the plowing by hard ZrO 2 ball characterized by abrasive and adhesive wear. Under normal test (UHMWPE ball conterface), all coatings showed significant improvement in wear resistance both in dry sliding and bovine serum lubrication. Both DLC and a-C films showed less surface damage than TiN film due to the self-lubricating phenomenon in dry sliding. TiN film showed the largest friction coefficient both in destructive and normal tests, devoting to the big TiN grains thus leading to much rougher surface and then a higher value. The self-lubricating film formed on DLC and a-C coating could also decrease their friction coefficients. The results indicated that three coatings revealed different wear mechanisms, and thick DLC or a-C film was more promising in application in lower stress conditions such as artificial cervical disk.

High-temperature Tribological Properties of Si3N4/TiC Ceramic with Bionic Surface Textures and DLC Coatings

High-temperature tribological properties of Si 3 N 4 /TiC ceramic with bionic surface textures and DLC coatings

Tribological performance of DLC-coated ceramics against cemented carbide under dry sliding conditions

Synergistic effect of surface textures and DLC coatings for enhancing friction and wear performances of Si3N4/TiC ceramic

High temperature solid/liquid lubrication behaviours of DLC films

High temperature tribology behavior of silicon and nitrogen doped hydrogenated diamond-like carbon (DLC) coatings

Microstructure and high-temperature tribological properties of Ti/Si co-doped diamond-like carbon films fabricated by twin-targets reactive HiPIMS

Influences of different temperatures on the mechanical properties and wear resistance against Ti6Al4V of Ti doped diamond-like carbon deposited on cemented carbide

High-temperature tribological properties of AlCrN coatings deposited on textured surfaces under dry friction

Tailoring the mechanical and high‐temperature tribological properties of Si‐DLC films by controlling the Si content

The High‐temperature Tribological Properties of Si‐DLC Films

Tribological behaviors of TiSiC coating in seawater environment

Tribological Properties of Ti3SiC2 Coupled with Different Counterfaces

Tribological behavior of a novel Si- and WC- co-reinforced a-C multilayer coating at 25– 500 °C

High temperature tribological performance and thermal conductivity of thick Ti/Ti-DLC multilayer coatings with the application potential for Al alloy pistons

ANALYSIS OF THE TRIBOLOGICAL PROPERTIES OF TiN/Si3N4 NANOCOMPOSITE COATING IN SLIDING CONTACT WITH CERAMIC, STEEL, AND POLYMER COUNTERPART

Tribological study of lubricious DLC biocompatible coatings

Tribological behaviour of TiB2-HfC ceramic tool material under dry sliding condition

Different tribological behaviors of titanium alloys modified by thermal oxidation and spraying diamond like carbon

The Tribological Behaviors of Three Films Coated on Biomedical Titanium Alloy by Chemical Vapor Deposition

Microstructure, Mechanical and Tribological Properties of CrSiC Coatings Sliding Against SiC and Al2O3 Balls in Water