Abstract:The phase equilibrium of Mg-Cu-Ca ternary system at 350 degrees C were investigated using thirteen key samples. Scanning electron microscopy (SEM) equipped with energy-dispersive spectroscope (EDS) was employed to investigate equilibrium relationships and phase compositions in alloy samples. Powder X-ray diffraction (XRD) technique was used to analyze the crystal structures of new found phases. Two unreported ternary phases, P1 and Mg25-xCu75Cax were observed and investigated for the first time. The compound P1 has a narrow solid homogeneity ranged from about Mg25Cu35Ca40 to Mg30Cu30Ca40 (in at. %). The solid solubility limit of the compound Mg25-xCu75Cax was found to be 8.03 <= x(Ca) <= 16.67 with constant value of about 75 at. % Cu at 350 degrees C. The 2q of fourteen diffraction peaks of new phase P1 were determined to be 23.0 degrees, 35.9 degrees, 37.3 degrees, 38.9 degrees, 42 degrees, 44 degrees, 47 degrees, 52.5 degrees, 54 degrees, 56.7 degrees, 62.3 degrees, 66.8 degrees, 68.2 degrees and 75.4 degrees. The 2q of ten diffraction peaks of the new compound Mg25-xCu75Cax were confirmed to be 20.5 degrees, 21.2 degrees, 34.7 degrees, 35.7 degrees, 42.3 degrees, 43.3 degrees, 44.8 degrees, 47.3 degrees, 50.5 degrees and 74.5 degrees. The maximum solid solubility of Ca in the terminal compound MgCu2 was found to be 8.83 at. % at 350 degrees C. Ternary maximum solid solubility of binary terminal compounds Mg2Ca, Mg2Cu, Cu5Ca and CuCa were less than 2 at. %. In addition, eight three-phase equilibrium relationships were determined in the present work. (C) 2019 Elsevier B.V. All rights reserved.

Phase Equilibria at 500ºc of the Mg-Nd-Zn System in the Region of < 50 At%Nd

Experimental determination of the phase equilibria of the Mg–Nd–Zn system at 320°C

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Phase Equilibria in the Ni-Sn-Zn System at 500°C

Microstructure and Mechanical Properties of Mg–4.5Zn–xNd (x=0, 1 and 2, Wt%) Alloys

Experimental Determination of the Phase Equilibrium in the Mg–Cu–Ca Ternary System at 350 °C

Isothermal section (500°C) of phase diagram of Nd-Al-Si ternary system

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Thermodynamic Modeling and Experimental Investigation of the Magnesium–neodymium–zinc Alloys

Effects of Nd on microstructures and properties at the elevated temperature of a Mg–0.3Zn–0.32Zr alloy

Isothermal Section of Ternary Sn-Zn-Ni Phase Equilibria at 250 °C

Effects of Nd on the microstructure of ZA52 alloy

Microstructure analysis of Mg-2.54Nd-0.26Zn-0.32Zr alloy

Phase composition for Zr(Mn1-xNix)2 alloys

Phase equilibria, crystal structure of δ1-MnZn9 and thermodynamic re-assessment of the Zn-Mn system

Phase equilibria of the Co-Ni-Zr system at 1198 K

Phase equilibria in the neodymium-cadmium binary system

Microstructure characterization on Mg-2Nd-4Zn-1Zr alloy during heat treatment

Isothermal Section of the Er–Co–Nd Ternary System at 773K

Experimental investigation and thermodynamic assessment of the Mg–Gd–Ag system focused on Mg-rich region

Phase equilibria in the ZrO 2 –Ta 2 O 5 –Nb 2 O 5 system: Experimental studies and thermodynamic modeling