Abstract:TbCo alloy films possess ferrimagnetic structure and high perpendicular anisotropy and have been proven to rapidly reverse their magnetic moments irradiated with an ultra-short pulse laser, which have the potential to use as all optical switching media [1–2]. In this paper, we have adopted a two-temperature model [3] and a general theoretical framework [4] to calculate the temperatures of the electron gas $( T_{\mathrm {e}})$ and the phonon $( T_{\mathrm {p}})$ and the magnetization dynamics of Tb 26 Co 74 films, respectively, and found that electron-phonon coupling factor (G) plays a significant influence on the $T_{\mathrm {e}}$ and magnetization reversal dynamics of TbCo films. In our simulation, the laser wavelength and pulse width, laser fluence are 560 nm, 100 fs and 15 J/m 2 , respectively. The G values vary from 1 to 10×10 17 W/m 3 . K. Fig 1 shows the time evolution of $T_{\mathrm {e}}$ and $T_{\mathrm {p}}$. $T_{\mathrm {e}}$ rapidly increases to the peak temperature within about 0.3ps and then decreases with different rates until reaching the same value as $T_{\mathrm {p}}$. TbCo films with a smaller G have a higher peak temperature of $T_{\mathrm {e}}$ and exhibit a slower cooling rate, and thus experience a longer heat exchange time between the electron gas and phonon. Fig 2 presents the computed time-resolved magnetization dynamics of Co- and Tb- sublattices. When G is just 1×10 17 W/m 3 . K, only the rapid demagnetization process occurs in Co- and Tb- sublattices and no magnetization reversal is observed due to the higher $T_{\mathrm {e}}$ and slower cooling rate. As G continues to increase, the demagnetization time of Co- sublattice rises slowly, but the initial reversal time of Co- sublattice drops gradually from 1.27ps to 0.66ps, which is attributed to the decreasing $T_{\mathrm {e}}$ and the increasing cooling rate of electron gas. Moreover, Tb- sublattice delays to reverse its magnetic moment with the increase of G perhaps owing to the lower $T_{\mathrm {e}}$ and the slower demagnetization of Tb- sublattice. Furthermore, although Co- and Tb- sublattices both generate magnetization reversal, the total magnetization reversal of Tb 26 Co 74 films does not occur within the timescale of 5ps and will happen after a relatively longer recovery of magnetic moments of Tb- sublattice.

Ultrafast single-pulse switching of Tb-dominant CoTb alloy

Ultrafast single-pulse all-optical switching in synthetic ferrimagnetic Tb/Co/Gd multilayers

From toggle to precessional single laser pulse switching

Laser Induced Ultrafast Magnetization Reversal in Tbco Film

Single-shot all-optical switching of magnetization in TbFe

All-optical Helicity-Independent Switching State Diagram in Gd - Fe - Co Alloys

All-optical helicity-independent switching state diagram in GdFeCo alloys

Role of spin-lattice coupling in ultrafast demagnetization and all optical helicity-independent single-shot switching in Gd<sub>1-<i>x</i>-<i>y</i></sub>Tb<i><sub>y</sub></i>Co<i><sub>x</sub></ i> alloys

Single shot ultrafast all optical magnetization switching of ferromagnetic Co/Pt multilayers

Unifying femtosecond and picosecond single-pulse magnetic switching in GdFeCo

In plane reorientation induced single laser pulse magnetization reversal in rare-earth based multilayer

Ultrafast Magnetization Manipulation Using Single Femtosecond Light and Hot‐Electron Pulses

Field-free all-optical switching and electrical read-out of Tb/Co-based magnetic tunnel junctions

Femtosecond Laser Heating Induced Ultrafast Magnetization Reversal in TbCo Films with Different Electron-Phonon Coupling Inter-Action

Roles of Heating and Helicity in Ultrafast All-Optical Magnetization Switching in TbFeCo

Single laser pulse induced magnetization switching in in-plane magnetized GdCo alloys

Single-shot multi-level all-optical magnetization switching mediated by spin-polarized hot electron transport

Criteria to observe single-shot all-optical switching in Gd-based ferrimagnetic alloys

Single pulse all-optical toggle switching of magnetization without gadolinium in the ferrimagnet Mn2RuxGa

Spin-Orbit-Torque Switching of Ferrimagnets by Terahertz Electrical Pulses

Magnetic and all-optical switching properties of amorphous Tb$_x$Co$_{100-x}$ alloys