Niobium Fluoride-Modified Hydrogen Evolution Reaction of Magnesium Borohydride Diammoniate

Yujie Lv,Bao Zhang,Haixiang Huang,Bogu Liu,Wei Lv,Jianguang Yuan,Guanglin Xia,Xuebin Yu,Dalin Sun,Ying Wu

DOI: https://doi.org/10.1016/j.jmst.2023.01.030

2023-01-01

Abstract:Metal borohydride ammoniates have become one of the most promising hydrogen storage materials due to their ultrahigh capacities. However, their application is still restricted by the high temperature of hy-drogen desorption and the release of ammonia. Here, to promote the dehydrogenation evolution and suppress the ammonia release, different amounts of NbF5 were introduced into Mg(BH4)2 center dot 2NH3. Com-pared to the pure Mg(BH4)2 center dot 2NH3, the Mg(BH4)2 center dot 2NH3-NbF5 composites exhibit lower onset dehydriding temperatures (53-57 degrees C) and higher dehydriding capacities (5.6 wt.%-8.2 wt.%) at below 200 degrees C, with the complete suppression of ammonia. In addition, 7.4 wt.% H2 could be released from Mg(BH4)2 center dot 2NH3 -5 mol% NbF5 composite at 200 degrees C within 20 min and the apparent activation energy is calculated to be 60.28 kJ mol-1, which is much lower than that of pure Mg(BH4)2 center dot 2NH3 (92.04 kJ mol-1). Mg(BH4)2 center dot 2NH3 should mechanochemically react with NbF5, forming dual-metal (Mg, Nb) borohydride ammoniate and spherical MgF2. The introduction of electronegative Nb cation results in-situ formation of (Mg, Nb) boro-hydride ammoniate towards a lower dehydrogenation temperature and a higher hydrogen release purity. The increased phase boundaries among the Mg(BH4)2 center dot 2NH3, dual-metal (Mg, Nb) borohydride ammoniate, and MgF2 phases further facilitate the hydrogen diffusion during the dehydrogenation of the composites.(c) 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.