Multiple Interface Ni(PO3)2-CoP4/CoMoO4 Nanorods for Highly Efficient Hydrogen Evolution in Alkaline Water/Seawater Electrolysis

Mei Yang,Shilin Zhang,Tian Wang,Beibei Shi,Jingyan Liu,Yili Tang,Zonglin Xu,Muhammad Tariq Sarwar,Aidong Tang,Huaming Yang

DOI: https://doi.org/10.1021/acssuschemeng.2c04034

IF: 8.4

2022-01-01

ACS Sustainable Chemistry & Engineering

Abstract:The key to the development of non-noble metal catalysts with high activity and durability for the hydrogen evolution reaction (HER) in alkaline water/seawater conditions is to construct multi-interface electrocatalysts. Herein, the CoMoO4 nanorod arrays grown on foam nickel (NF) was first prepared by a hydrothermal method. Then, Ni(PO3)(2)-CoP(4 )with multi-interface was prepared by soaking the nanorod arrays into a nickel nitrate solution and then by phosphating via chemical vapor deposition. The Ni(PO3)(2)-CoP4/CoMoO4/NF electrode exhibits superior HER electrocatalytic performance under alkaline conditions with an ultralow overpotential of 79 mV@100 mA.cm(-2), which outperforms other reported earth-abundant transition-metal phosphide catalysts. It also maintains long-term durability in alkaline water/seawater electrolytes in 60 h at a constant 100 mA.cm(-2). In the alkaline natural seawater electrolyte, Ni(PO3)(2)-CoP4/ CoMoO4/NF (-)||NiFe LDH (+) pair has good long-term stability of 60 h for the voltage of only 1.60 V@100 mA.cm(-2). The excellent performance is attributed to the plentiful active sites and the rapid electron-transfer rate. This work affords a new path to rationalize the design strategy of low-cost and multi-interface 3D catalysts for alkaline water/seawater electrolysis.