Preparation of CuFeO2@PVP for the photo-electro-Fenton degradation of ofloxacin

ZHANG Lidong,FU Wenxian,HUO Siyue,LI Jie,GAO Mengchun

DOI: https://doi.org/10.12030/j.cjee.202211125

2023-01-01

Abstract:The CuFeO 2 @PVP catalyst with rich oxygen vacancies was synthesized via a simple one-step hydrothermal method with polyvinylpyrrolidone as modifier. The successful synthesis of the catalyst and its morphology and microstructure were confirmed by XRD, FT-IR, SEM, TEM and EPR methods. UV-vis DRS,PL, EIS and IT were used to confirmed that CuFeO 2 @PVP has better photocatalytic activity and photoelectrochemical properties than CuFeO 2 . The results of degradation experiments with different systems showed that the degradation efficiency by CuFeO 2 @PVP in photo-electro-Fenton system increased significantly,which was 1.79 times as much as pure CuFeO 2 . The removal rate by photo-electro-Fenton system was 66.8%,66.5% and 9.3% higher than photocatalysis, electrocatalysis and electro Fenton system, respectively, which indicated that there was a synergistic effect among the visible light, electro and heterogeneous catalyst. The effects of catalyst dosage, current density, solution pH values and coexistence ions on the degradation of OFX were further discussed. The removal rate for 10 mg·L -1 OFX was 94.3% after 120 min oxidation at catalyst dosage of 0.4 g·L -1 and current density of 4 mA/cm~2. At pH 5-9, OFX degradation was inhibited, while at pH 3-3.6, the degradation was almost unchanged. Cl - had a slight acceleration effect on OFX degradation, while NO 3 - ,PO 4 3- and CO 3 2- inhibited the reaction. In addition, the degradation efficiency of CuFeO 2 @PVP decreased by 13.8% after 5 cyclic degradation experiments, indicating that it has good stability. The results of radical quenching experiment and electron paramagnetic resonance showed that ·OH was the main active radical, and the possible degradation mechanism was inferred based on the above results.