3D Porous and Li-rich Sn–Li Alloy Scaffold with Mixed Ionic-Electronic Conductivity for Dendrite-Free Lithium Metal Anodes

Longtao Ren,Xin Cao,Yan Wang,Mingyue Zhou,Wen Liu,Haijun Xu,Henghui Zhou,Xiaoming Sun

DOI: https://doi.org/10.1016/j.jallcom.2023.169362

IF: 6.2

2023-01-01

Journal of Alloys and Compounds

Abstract:The rechargeable lithium metal batteries (LMBs) have attracted considerable attention as the promising candidates of next-generation energy storage technologies, but they often suffer from the dendrite growth and short lifespan, especially at high current densities and low negative/positive capacity (N/P) ratios. Herein, a facile, low-cost, and scalable route was developed to prepare the 3D porous and Li-rich Sn–Li alloy scaffolds to ensure homogeneous Li plating/stripping under high current density. The Li-rich Sn–Li alloy scaffolds exhibit considerable affinity with Li, which can not only guide the uniform Li deposition without dendrites formation, but also re-store active Li to supplement the irreversible Li loss, thus contributing to the long-term cycling stability. As a result, Li||Cu cell maintains an average Coulombic efficiency of 96.5 % even at a current density of 5 mA cm−2. When coupling this anode with LFP cathode, the thus-assembled full cells achieve a superior capacity retention of 87 % over 400 cycles at 5 C. Stable cycling of LMBs with a low N/P capacity ratio of 1.5 is also demonstrated, showing the prominence of this strategy for developing high-energy-density LMBs.