Strongly Luminescent and Highly Stable CsPbBr3/Cs4PbBr6 Core/shell Nanocrystals and Their Ultrafast Carrier Dynamics

Chenxu Wang,Lihe Yan,Jinhai Si,Tianyu Huo,Xun Hou

DOI: https://doi.org/10.1016/j.jallcom.2023.169272

IF: 6.2

2023-01-01

Journal of Alloys and Compounds

Abstract:All-inorganic lead halide perovskites nanocrystals (NCs) have been demonstrated to be promising candi-dates for optoelectronic devices, but preparing perovskite NCs with high photoluminescence quantum yields (PLQYs) and excellent stability has been a challenge. In this work, CsPbBr3/Cs4PbBr6 core/shell NCs with a PLQYs of 87.23% and long-term stability in ambient environments was prepared by room tem-perature inverse microemulsion method. The excellent stability of the sample was attributed to the pro-tection of Cs4PbBr6, and higher PLQYs could be owing to the passivation effect of the core/shell structure. To illustrate the distribution of photogenerated carrier in the core/shell structure, a confined excitons model was proposed based on time-resolved PL and temperature dependent PL measurements. Femtosecond time-resolved transient absorption spectra measurements were performed upon different excitation wa-velength to unveil the photogenerated carrier dynamics in core/shell NCs. Upon 300 nm excitation, a carrier transfer process with the time of 3.18 ps from shell to core layer was observed. Furthermore, both two-and three-photon absorption PL was discovered in core/shell NCs, further verifying the carrier transfer process.(c) 2023 Elsevier B.V. All rights reserved.