Abstract:The curved woven lattice truss sandwich (CWLTS) panels were developed, made, and tested as a type of lightweight composite structures utilized in aerospace, shipbuilding, rail transport and building engineering. Three‐point bending experiments indicated the effects of curving and foam‐filling on the deformation, damage, failure, and energy absorption under cylindrical and plated loadings. The woven lattice truss sandwich panels (WLTSPs) have been studied much, and this article proposes a new structure (curved woven lattice truss sandwich [CWLTS] panels). CWLTS were designed, made, and tested. The foam‐filling technique was applied to strengthen the CWLTS. Curving and foam‐filling effects to the deformation, damage, failure, and energy absorption under cylindrical and plated loadings were revealed by three‐point bending experiments. Under cylindrical loading, foam‐filling can effectively increase the load capacity, especially the CWLTS‐A. The load‐bearing capacity of the plated loading is greater than that of the cylindrical loading, and the phenomenon is significantly improved after foam filling, except for the central angle of 60° and the CWLTS‐A of 44.05°. Foam‐filling changes failure from core‐shearing to face fracture. For foam‐filled panels, the change in loading pattern results in energy absorption increase of 2.45 times for CWLTS‐B and 2.86 times for CWLTS‐A. Plated loading approximately doubles the peak load and energy absorption with two plastic hinges. The effect of foam filling on the mean crush force of the CWLTS plated loading is greater. The mechanical and energy absorption properties of the CWLTS can be improved by changing the loading mode and using foam filling, effectively increasing the applicability. Highlights Curved woven lattice truss sandwich panels were designed, made, and tested. Foam‐filling method greatly improves the bearing capacity of the CWLTS panels. Plated loading much increases the bearing capacity and energy absorption. The impact of curvature on mechanical performances is not immediately apparent.

Manufacturing and Mechanical Testing of Woven Lattice Truss C-sandwich Radome Composites

Mechanical Behavior of Carbon Fiber Reinforced Polymer Composite Sandwich Panels with 2-D Lattice Truss Cores

Effects of lattice configuration on multifunctionality of C-sandwich radome

Double-layer Woven Lattice Truss Sandwich Composite for Multifunctional Application: Design, Manufacture and Characterization

Sandwich-Walled Cylindrical Shells with Lightweight Metallic Lattice Truss Cores and Carbon Fiber-Reinforced Composite Face Sheets

Foam-Filled Double-Layer Woven Lattice Truss Sandwich Panels: Manufacturing, Testing and Composite Effects

Manufacturing and Flexural Testing of Woven Lattice Sandwich-Ply Laminate Composites

Manufacturing and Testing of a CFRC Sandwich Cylinder with Kagome Cores

Lattice Truss Core Sandwich Structures With Al Lattice Truss Core And Cfrp Composite Fachesheets Under Impact Loads

Fabrication and Testing of Carbon Fiber Reinforced Truss Core Sandwich Panels

Fabrication And Axial Compressive Behavior Of Composite Sandwich Cylindrical Shells With Pyramidal Lattice Truss

Curved woven lattice truss sandwich panels strengthened by foams: Designing, manufacturing, and testing

Fabrication and mechanical behaviors of corrugated lattice truss composite sandwich panels

Mechanical behaviours of composite sandwich panel with strengthened pyramidal truss cores

PROCESSES IN THE STUDY ON NOVEL COMPOSITE SANDWICH PANELS WITH LATTICE TRUSS CORES

Mechanical Response of All-Composite Pyramidal Lattice Truss Core Sandwich Structures

Mechanical Behaviour of CFRP Sandwich Structures with Tetrahedral Lattice Truss Cores

Structural Responses of All-Composite Improved-Pyramidal Truss Sandwich Cores

A Novel Carbon Fiber Reinforced Lattice Truss Sandwich Cylinder: Fabrication and Experiments

Buckling and post-buckling of anisogrid lattice-core sandwich plates with nanocomposite skins

FABRICATION AND MECHANICAL RESPONSE OF CARBON FIBER SANDWICH PANELS WITH PYRAMIDAL TRUSS CORES