Heat-pattern Induced Non-Uniform Radial Microstructure and Properties of Ti-6Al-4V Joint Prepared by Rotary Friction Welding

Feng Jin,Haodong Rao,Qian Wang,Guodong Wen,Pu Liu,Jiatao Liu,Junjun Shen,Jinglong Li,Jiangtao Xiong,Ninshu Ma

DOI: https://doi.org/10.1016/j.matchar.2022.112536

IF: 4.537

2023-01-01

Materials Characterization

Abstract:Heat-pattern (HP) induced non-uniform radial microstructure and properties of rotary friction welded Ti-6Al-4 V joint was focused in this study, the formation mechanism of which was clarified by beta-reconstruction. The results show that Ti-6Al-4 V friction welded heat-pattern at different rotational speeds can be generally separated into 'glass-like' HP and 'scissor-like' HP. According to the results of beta-reconstruction, the radial microstructures of 'glass-like' HP and 'scissor-like' HP are deformed alpha grains -> deformed alpha grains and lamellar alpha' laths -> lamellar alpha' laths corresponding to center -> 1/2R -> periphery respectively, where lamellar alpha' laths at periphery of 'scissor-like' HP have similar orientations to form alpha' colony. Deformed alpha grains at center zone make the strength higher than that of base metal (BM) and share the similar morphology of BM compared with the lamellar alpha' laths, to get the highest elongation among the three regions of center, 1/2R and periphery, reaching near 80% of BM. Whereas, lamellar alpha' laths at periphery share a coarser size than that of the center zone, the strength of which is reduced and close to the BM. Compared with the deformed alpha grains, lamellar alpha' laths are quite different from BM in morphology, which causes a significant reduction in elongation to only 62.1% of BM. Aggravating the issue further, the elongation of 'scissor -like' HP is reduced to only 50.3% of BM at periphery because of alpha' colony. Therefore, the strength and elongation of the joint decrease gradually from center to periphery.