Abstract:This study was aimed to prepare a silk fibroin (SF)/chitosan (CS)/nano-Hydroxyapatite (n-HAp) composite scaffold for repair of cartilage damage. A four-layer bionic scaffold SF/CS/n-HAp was constructed by cryogenic freezing and forming. Sodium Tripolyphosphate (STPP) was used as a cross-linking agent to post-process the scaffold to improve the mechanical strength of the scaffold. The various materials prepared were characterized. The SF/CS/n-HAp scaffold prepared in this study was cream-colored cylindrical and elastic. It can show variability after external force was applied, and can be restored to its original appearance after elimination of the external force. The diameter of the scaffold was 5 cm, and the total thickness was about 1 cm. The scanning electron microscope (SEM) results showed that the surface of the scaffold material was smooth, the pore size changed gradually, and the connectivity among the holes was good. The pore size distribution of the entire scaffold material was between 100 μ m∼300 μ m, and the pore size range was suitable for the adhesion, expansion, and migration of chondrocytes and osteoblasts. The mechanical performance test results showed that the composite scaffold had a compression modulus of 706 kPa, which can meet the mechanical performance requirements for repair of smaller articular cartilage damage. In addition, the porosity of each layer of the scaffold was more than 91%, which was conducive to the adhesion of cells on the surface of the material. The cell experiment results revealed that the composite scaffold material was beneficial to the growth and proliferation of cells. Under osteogenic and chondrogenic induction culture, bone marrow stromal cells (BMSCs) can differentiate in the direction of osteogenesis and cartilage. The results of animal experiments revealed that the SF/CS/n-HAp material group showed better effect than the blank control group in repairing rat cartilage defects, and the Wayne score and O’Driscoll score were also significantly higher than the blank control group. This suggested that the biomimetic scaffold SF/CS/n-HAp prepared in this study showed good physical properties and biocompatibility, and had certain prospects in the application of repairing cartilage damage.

Regenerated Silk Fibroin Hydrogel with Laponite/Polydopamine Composite Nanoparticles

Self‐Healing Silk Fibroin‐Based Hydrogel for Bone Regeneration: Dynamic Metal‐Ligand Self‐Assembly Approach

Enhancing Mechanical Properties of Silk Fibroin Hydrogel Through Restricting the Growth of Β-Sheet Domains

Enhancing the Gelation and Bioactivity of Injectable Silk Fibroin Hydrogel with Laponite Nanoplatelets

Progress in Silk Fibroin Based Composite Scaffold/Hydrogel: Silk Fibroin/PEG Hydrogel for the RPE Regeneration a Promising Biomaterial for Clinical Application

Silk–Inorganic Nanoparticle Hybrid Hydrogel as an Injectable Bone Repairing Biomaterial

Preparation of silk fibroin/hyaluronic acid hydrogels with enhanced mechanical performance by a combination of physical and enzymatic crosslinking

Long-Lasting Thixotropic Natural Polymeric Hydrogel Based on Silk Nanofibrils.

Physically Crosslinked Biocompatible Silk‐Fibroin‐Based Hydrogels with High Mechanical Performance

Progress in Hydrogels Based on Regenerated Silk Fibroin

Silk fibroin hydrogel membranes prepared by a sequential cross-linking strategy for guided bone regeneration

Preparation of Silk Fibroin/Chitosan/Nano-Hydroxyapatite and Its Effect on the Repair of Cartilage Damage in Rats

Injectable Ultrasonication-Induced Silk Fibroin Hydrogel for Cartilage Repair and Regeneration

Preparation of bacterial cellulose/silk fibroin double-network hydrogel with high mechanical strength and biocompatibility for artificial cartilage

Biosynthesizing lignin dehydrogenation polymer to fabricate hybrid hydrogel composite with hyaluronic acid for cartilage repair

Preparation of silk fibroin/hyaluronic acid composite hydrogel based on thiol-ene click chemistry

Enhanced Osteogenesis of Bone Marrow-Derived Mesenchymal Stem Cells by a Functionalized Silk Fibroin Hydrogel for Bone Defect Repair.

Multifunctional Hydrogel Based on Silk Fibroin Promotes Tissue Repair and Regeneration

Construction of Injectable Silk Fibroin/polydopamine Hydrogel for Treatment of Spinal Cord Injury

Synthetic/natural Blended Polymer Fibrous Meshes Composed of Polylactide, Gelatin and Glycosaminoglycan for Cartilage Repair.

GOx/Hb Cascade Oxidized Crosslinking of Silk Fibroin for Tissue-Responsive Wound Repair