Long-Pursued Structure of Au23(S-Adm)16 and the Unexpected Doping Effects
Lei Feng,Ze-Min Zhu,Ying Yang,Zongbin He,Jiafeng Zou,Man-Bo Li,Yan Zhao,Zhikun Wu
DOI: https://doi.org/10.3866/pku.whxb202305029
2023-01-01
Acta Physico-Chimica Sinica
Abstract:Metal nanoclusters are rising stars in material science , and one advantage is their atomically precise tunability. It is well known that metal doping can efficiently modify the properties of metal nanoclusters. In particular, without altering the parent nanocluster framework, doping a single heterometal atom can tailor the properties of metal nanoclusters and aid investigations of the structure-property relationship of metal nanoclusters. To our knowledge, the simultaneous synthesis of a single heterometaldoped nanocluster and its parent nanocluster is challenging and has not been previously reported; however, this is highly desirable because it can prevent the influence of trace impurities and allow comparison between doped and undoped nanoclusters. The single Cd-doped gold nanocluster Au 22 Cd 1 (S-Adm) 16 (S-Adm = 1-adamantanethiolate) has been previously synthesized and structurally elucidated. However, the structure of the parent nanocluster, Au 23 (S-Adm) 16 , remains unknown, inspiring this investigation. In this study, we synthesized Au 23 (S- Adm) 16 and its single -doped Au 22 Cd 1 (S-Adm) 16 nanocluster in one pot for the first time, and we resolved their structures using single -crystal X-ray crystallography. The structure of Au 22 Cd 1 (S-Adm) 16 is similar to that of Au 23 (S-Adm) 16 except that a kernel Au atom in Au 23 (S-Adm) 16 is replaced with a Cd atom. This Cd replacement causes the kernel Au & horbar;Au bond length to increase owing to the loosening of the original closely packed structure. In contrast to prior reports, Au 23 (S-Adm) 16 is surprisingly more stable than Au 22 Cd 1 (S-Adm) 16 , as determined via ultraviolet visible -near infrared (UV-Vis-NIR) spectroscopy at 80 degrees C. This stability was attributed to the decrease in the kernel Au & horbar;Au bond length. Although the maximum absorption of Au 22 Cd 1 (S-Adm) 16 slightly red -shifted from 605 to 608 nm after Cd doping, the molar extinction coefficient of Au 23 (S-Adm) 16 at 605 nm was approximately twice that of Au 22 Cd 1 (S-Adm) 16 at 608 nm. Thus, the increase in kernel Au & horbar;Au bond length may decrease the photoexcitation electron transfer efficiency owing to lengthening of the photoexcitation electron transfer pathway. As further support for this opinion, although the two nanoclusters showed similar emission profiles and maxima (750 nm for Au 23 (S-Adm) 16 and 760 nm for Au 22 Cd 1 (S-Adm) 16 ), they exhibited obvious emission intensity differences. Specifically, the quantum yield of Au 23 (S-Adm) 16 (approximately 3.160 x 10 -5 ) was found to be 1.13 times that of Au 22 Cd 1 (S-Adm) 16 (approximately 2.793 x 10 -5 ). Thus, the stability and absorption and emission intensities correlate with the kernel Au & horbar;Au bond length. This study shows that two metal nanoclusters with slight structural differences can exhibit different properties in terms of optical and thermal stability, providing a good reference for studying their structure-property relationships.