Photoinduced Strain in Organometal Halide Perovskites.

Bing Li,Yinan Jiao,Shengjian Qin,Ye Wang,Huan Liu,Rui Li,Weizhong Hao,Hao Li,Yuanhua Xia,Xiangyu Li,Jinjin Zhao
DOI: https://doi.org/10.1021/acs.jpclett.2c03573
IF: 6.888
2023-01-01
The Journal of Physical Chemistry Letters
Abstract:There is a lack of fundamental understanding of mechano-electro-optical multifield coupling for organometallic halide perovskites (OHPs). In this study, the effect of light irradiation on OHPs' mechanical properties was investigated by atomic force microscopy. In the dark, an MAPbI3 film was dominated by grains with a Young's modulus of approximately 5.94 GPa, which decreased to 2.97 GPa under light illumination. The photoinduced strain distribution within the polycrystalline MAPbI3 film was not uniform, and the maximum strain generated inside individual grains was 5.8%. Furthermore, the illumination-induced strain promoted the formation of ferroelastic domains. The Young's modulus of one domain increased from 8.99 to 25.27 GPa, whereas the Young's modulus of an adjacent domain decreased from 14.9 to 1.30 GPa. According to the density-functional-theory calculations, the observed photoinduced strain-promoted variations in mechanical properties were caused by the reversible migration of MA+ cations. These findings can help establish the relationship among the mechanical-chemical-optoelectronic characteristics of OHPs.
What problem does this paper attempt to address?