Abstract:In this paper, the Ti-6Al-4V(TC4) alloy specimens pre-coated with Ti-Cu-Al multilayer films were plasma nitrided at different temperatures (673K-823K), and their microstructure and mechanical properties were studied. Surface hardness changes induced by pre-coating combined with plasma nitriding were also analyzed and correlated with microstructural features and elemental distribution. Ti-Cu-Al multilayer films with clear interfaces on deformed TC4 alloy were fabricated. The multilayer structure survived after nitriding, and a thick gradient nitrided layer with a gradient distribution of N elements was formed. The bonded nitride on the surface provides high hardness, reaching 948HV at 723K. In addition, the nitride TC4 alloy's wear resistance exhibits a significant improvement compared with the untreated specimen, especially at 823K, the mass wear rate decreased by more than 80%. It is mainly attributed to the N/metal element gradient distribution of the thick nitride layer. The nitriding behavior of α-Ti/Cu/Al was investigated by first-principles calculations. According to the thermodynamic calculation results, N atoms preferentially occupy the octahedral interstitial sites of α-Ti and the tetrahedral interstitial sites of Al. It is worth noting that N atoms have poor thermodynamic stability in Cu, which is consistent with the experimental results. The calculated elastic properties agree with the experimental cross-sectional hardness results, showing a smooth decreasing trend of the complex modulus and hardness on the micrometer length scale and explaining the improved structure performance. These results may provide crucial inspirations for future experimental work preparing high-performance nitrided layers.

Columnar and Nanocrystalline Combined Microstructure of the Nitrided Layer by Active Screen Plasma Nitriding on Surface-Nanocrystalline Titanium Alloy

Microstructure characterization and evolution mechanism of titanium during laser surface nitriding

Modification mechanism of Ti-6Al-4V alloy with pre-coated Ti-Cu-Al multilayer film treated by ion nitriding: Experiments and first-principles calculations

Low-temperature plasma nitriding at 500°C on surface-nanocrystalline Ti–4Al–2V alloy

Attempt to achieve low temperature plasma nitriding on Ti-6Al-4V alloy by surface nanocrystallization

The microstructural characterization of the nitrided layers prepared by direct current nitrogen arc

Plasma Nitridation and Mechanical Properties of Pure Titanium Casts

In situ formation of TiN coating on TA2 pure titanium via laser surface nitriding

Characterization and electrochemical behavior of a multilayer-structured Ti–N layer produced by plasma nitriding of electron beam melting TC4 alloy in Hank's solution

The plasma nitriding treatment of TiN/TiCN multilayer films

Microstructures and wear resistance of titanium-assisted nitrided layers on aluminum substrate

Anisotropic Phase Transformation Mechanism on Coarse-Grained and Fine-Grained Pure Titanium at Low-Temperature Plasma Nitriding

Microstructure evolution and mass transfer behavior during multi-pass laser surface nitriding process on titanium alloy

Laser nitridation on Ti-6.5Al-3.5Mo-1.5Zr-0.3Si titanium alloy

Microstructural Characterization And Formation Mechanism Of Nitrided Layers On Aluminum Substrates By Thermal Plasma Nitriding

High Temperature Plasma Nitriding to Modify Ti Coated C17200 Cu Surface: Microstructure and Tribological Properties

Plasma Spray Deposition Enhancement of Titanium Nitride Layer Using Nitrogen-Contained Plasma Irradiation of Titanium Substrate as a Pre-spraying Method

Nanocrystallite Superhard Titanium Nitride Film In Multi-Arc Ion Plating

Microstructure and Mechanical Properties of Multiphase Coating Produced by Plasma Nitriding Ti Coated Gb-5083 Aluminum Alloy

Plasma Nitriding of 20crmo Steel with Nanostructured Surface Layer

Synthesis of TiN/Ti3Al composite coatings on Ti6Al4V alloy by plasma spraying and laser nitriding