Enhanced Proton Conductivity and CO2-tolerance of Intermediate-Temperature Protonic Ceramic Fuel Cell with Lanthanum Tungstate-Based Composite Cathode

Xiaoyu Wang,Meijuan Fei,Chuan Zhou,Wenhuai Li,Xixi Wang,Xuanxuan Shen,Dongliang Liu,Wanqing Chen,Peng Chen,Guancong Jiang,Ran,Wei Zhou

DOI: https://doi.org/10.1016/j.compositesb.2023.110565

IF: 11.322

2023-01-01

Composites Part B Engineering

Abstract:Despite the low activation energy for proton diffusion under protonic ceramic fuel cell (PCFC) operation, the high-performance PCFC is still limited by the low proton conductivity of most cathode materials. A decrease in cathode acidity can enhance proton affinity; however, the severe CO2-tolerance associated with the doping of alkaline earth metals in perovskite oxides is also a challenge. Herein, a proton conducting oxide La5.5W0.45-Mo0.4Nb0.15O11.25-delta (LWMN), which possesses excellent chemical stability under a CO2-containing atmosphere, is composited with Sr2Sc0.1Nb0.1Co1.5Fe0.3O6-delta (SSNCF) as the PCFC cathode. A 3 wt% alkali earth ion-free oxide LWMN composite in the cathode material can strengthen proton diffusion while weakening CO2 adsorption. Thus, in wet air containing CO2, the symmetrical cell based on the 3 wt% LWMN-SSNCF achieved a linear degradation rate of ASRs of 1.33 x 10-3 omega cm2 min-1 for the first 3 h, which was lower than the 2.15 x 10-3 omega cm2 min-1 achieved by the symmetrical cell based on the single-phase SSNCF cathode. Furthermore, the PCFC based on the composite cathode shows an improved performance of 1.114 W cm-2 at 650 degrees C due to its superior proton conduction. This strategy endowed the cathode with superior proton diffusion as well as low CO2 adsorption.